DAI-EL G-723F
- Chemical Family
- Fluoropolymers
DAI-EL G-723F, available in solid and sheet forms, presents an odorless composition with good mold-release properties. Designed for automotive and industrial applications, it serves in fuel entrance cover seals and O rings. This white-colored product aligns with clean standards and utilizes compression molding processing methods.
Properties
- Physical Form
- Sheets, Solid
- Sheets
- Solid
Product families
- Powertrain & UTH
- Equipment & Parts
Other characteristics
- Brand
- DAI-EL
- Color
- White
- End Uses
- Fuel Entrance Cover Seal, O Rings
- Features
- Good Mold Release, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Tensile Strength
- 14.0 - 14.0 MPa
- Note
*1 The above values are representative and not guaranteed.; *2 [Formula] DAI-EL G-723F: 100 phr, MT carbon black (N990): 20 phr, Calcium hydroxide: 6 phr, Magnesium Oxide (high-active): 3 phr, [Curing condition] Press cure: 10min@170°C, Post cure: 24hrs@230°C.; *3 P-24 O-ring.
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Technology
- Elastomers
- Benefits
DAI-EL G-723F is a cure-incorporated copolymer of vinylidene fluoride and hexafluoropropylene which is suitable for compression molding.. As it contain internal mold release agent, it is released from the mold easily.
- Product Families
- Elastomers — Parts & Shapes
- Additives Included
- Mold Release Agent
- Material Features
- Good Mold Release
- Odorless
- Packing Specification
- 20kg
- Plastics and Elastomers End Uses
- Fuel Entrance Cover Seal
- O Rings
- Safety Information
Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.. This product has been developed for industrial purpose and we shall not guarantee the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
- Plastics and Elastomers Processing Methods
- Compression Molding
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 200°C,70 hours, 25% Compression*³) | 20 | % | — |
| Elongation (at break) | 220 | % | ASTM D412 |
| Fluorine Content | 66 | mass% | — |
| Hardness (at 3 sec) | 67 | Shore A | ASTM D2240 |
| Hardness (at Peak) | 72 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10) | -18 | °C | ASTM D1329 |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 62 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 41 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.81 | — | ASTM D792 |
| Tensile Strength | 14 | MPa | ASTM D412 |
Table 2 of 2
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 4.4 | MPa | ASTM D412 |