DAI-EL G-211
- Chemical Family
- Fluoropolymers
DAI-EL G-211, available in sheet form, stands out with good adhesion, mechanical properties, and an odorless nature. This white-colored product targets applications like O rings, fuel entrance cover seals, and gaskets in the automotive sector. Specifically designed for automotive exterior and body applications, it follows chemical cure methods and processing through compression molding. Its solubility in lower ketones and esters enhances its compatibility with various industrial processes.
Properties
- Physical Form
- Sheets
Product families
- Exterior & Body
- Powertrain & UTH
Other characteristics
- Brand
- DAI-EL
- Color
- White
- End Uses
- Fuel Entrance Cover Seal, Gaskets, O Rings
- Features
Good Adhesion, Good Mechanical Properties, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Tensile Strength
- 16.2 - 16.2 MPa
- Note
*1 The above values are representative and not guaranteed.. *2 [Formula] DAI-EL G-211: 100 phr, MT carbon black (N990): 20 phr, Magnesium Oxide (high-active): 15 phr, Vulcanizing agent V-3: 5 phr, [Curing condition] Press cure: 20min at 190°C, Post cure: 24hrs at 200°C.
- Markets
- Automotive & Transportation
- Soluble In
- Lower ketones and esters
- Cure
- Chemical Cure
- Technology
- Elastomers
- Product Families
- Elastomers — Parts & Shapes
- Material Features
- Good Adhesion
- Good Mechanical Properties
- Odorless
- HIGHLIGHTS
DAI-EL G-211 is a diamine type terpolymer of vinylidene fluoride, tetrafluoroethylene and hexafluoropropylene which is suitable for compression molding.. It offers excellent adhesion to metal and mechanical properties.
- Packing Specification
- 20 Kg
- Plastics and Elastomers End Uses
- Fuel Entrance Cover Seal
- Gaskets
- O Rings
- Safety Information
Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.. This product has been developed for industrial purpose and we shall not guarantee the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
- Plastics and Elastomers Processing Methods
- Compression Molding
Technical data
Table 1 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Fluorine Content | 68.5 | mass% | — |
| Mooney Viscosity (ML₁₊₁₀)(at 121°C) | 47 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀)(at 140°C) | 23 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.87 | — | ASTM D792 |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 4.3 | MPa | ASTM D412 |
| Elongation (at break)*² | 240 | % | ASTM D412 |
| Hardness (at 3 sec)*² | 75 | Shore A | ASTM D2240 |
| Hardness (at Peak)*² | 78 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10)*² | -15 | °C | ASTM D1329 |
| Tensile Strength*² | 14.7 | MPa | ASTM D412 |