DAI-EL G-701
- Chemical Family
- Fluoropolymers
DAI-EL G-701, in solid form, is characterized by a good compression set, mechanical properties, and an odorless nature. Targeting automotive and industrial applications, it finds use in O rings. With chemical cure and compression molding as its preferred methods, this product is soluble in lower ketones and esters, ensuring optimal performance.
Properties
- Physical Form
- Solid
Product families
Applications
- Powertrain & UTH
- Equipment & Parts
Product Families
- Fluoroelastomers
Other characteristics
- Brand
- DAI-EL
- Features
Good Compression Set, Good Mechanical Properties, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Processing Methods
- Compression Molding
- Note
*1 The above values are representative and not guaranteed. *2 [Formula] DAI-EL G-701: 100 phr, MT carbon black (N990): 20 phr, Calcium hydroxide: 6 phr, Magnesium Oxide (highactive): 3 phr [Curing condition] Press cure: 10min at 170°C, Post cure: 24hrs at 230°C. *3 P-24 O-ring.
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Cure
- Chemical Cure
- Technology
- Elastomers
- Material Features
- Good Compression Set
- Good Mechanical Properties
- Odorless
- HIGHLIGHTS
DAI-EL G-701 is a curing-incorporated copolymer of vinylidene fluoride and hexafluoropropylene.; It offers excellent compression set and mechanical properties and is suitable for seal material.; It is a bisphenol curable standard type DAI-EL which is suitable for compression molding of simple shaped molding such as O-ring.
- Packing Specification
- 20 Kg
- Plastics and Elastomers End Uses
- O Rings
- Safety Information
Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.. This product has been developed for industrial purpose and we shall not guarantee the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
- Plastics and Elastomers Processing Methods
- Compression Molding
Technical data
Table 1 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Fluorine Content | 66 | mass% | — |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 55 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀)(at 121°C) | 41 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.81 | — | ASTM D792 |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 5.2 | MPa | ASTM D412 |
| Compression Set (70hours at 200°C, 25% Compression*³)*² | 17 | % | — |
| Elongation (at break)*² | 190 | % | ASTM D412 |
| Hardness (at 3 sec)*² | 68 | Shore A | ASTM D2240 |
| Hardness (at Peak)*² | 72 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10)*² | -18 | °C | ASTM D1329 |
| Tensile Strength*² | 14 | MPa | ASTM D412 |