Neoflon PFA TC-7409BK
- Chemical Family
- Fluoropolymers
Neoflon PFA TC-7409BK is identified as a solventborne coating, showcases outstanding characteristics such as abrasion resistance and high hardness. Neoflon PFA TC-7409BK is a liquid physical form, this coating is well-suited for applications requiring durability and toughness.
Properties
- Physical Form
- Liquid
Product families
- Protective Coatings
Other characteristics
- Brand
- Neoflon
- Features
- Abrasion Resistant, High Hardness
- Product Type
- Solventborne Coating
- Note
The above values in properties are typical and not guaranteed.
- Technology
- Ready-to-Use Products
- HIGHLIGHTS
Polyflon PTFE TC - 7400 grade is a solvent based PTFE coating.. Polyflon PTFE TC - 7409BK makes a black coating layer displaying hardness and abrasion resistance and hardness. It can be sintered at lower temperature (150 - 200°C).
- Ready to Use Product Features
- Abrasion Resistant
- High Hardness
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
Technical data
Table 1 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Film Appearance | Black | — | — |
| Solid Content | 34 | mass% | — |
| Specific Gravity of Coating | 0.98 | — | — |
| Viscosity (at 25°C) | 16 | seconds | Ford Cup No.4 |
Table 2 of 2
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Chemical Resistance (for 16hours, at 25°C, Hydrochloric acid) | No change | — | — |
| Chemical Resistance (for 16hours, at 25°C, Methanol) | No change | — | — |
| Chemical Resistance (for 16hours, at 25°C, Nitric acid) | No change | — | — |
| Chemical Resistance (for 16hours, at 25°C, Sodium hydroxide) | No change | — | — |
| Chemical Resistance (for 16hours, at 25°C, Sulfuric acid) | No change | — | — |
| Chemical Resistance (for 16hours, at 25°C, Xylene) | Swelling 1.0% | — | — |
| Contact Angle (Hexadecane, at 25°C) | 35 - 41 | Degree | Contact Angle Meter |
| Contact Angle (Water, at 25°C) | 92 - 96 | Degree | Contact Angle Meter |
| Friction Coefficient (Bauden leben type, Steel ball 8mmφ, Linear velocity 0.27cm/s, Loading 1.0kg) | 0.04 - 0.08 | — | Bauden leben steel sheet |
| Maximum Temperature | 160 | °C | — |
| Pencil Hardness (After immersed in boiled water for 500hours) | H | — | Mitsubishi Uni |
| Pencil Hardness (at 25°C) | 3H | — | Mitsubishi Uni |