Neoflon PFA TC-7400CR
- Chemical Family
- Fluoropolymers
Neoflon PFA TC-7400CR, categorized as a solventborne coating that stands out with its impressive attributes of abrasion resistance and high hardness. In liquid form, this coating product ensures reliable protection and durability in applications requiring resistance to wear and hardness.
Properties
- Physical Form
- Liquid
Product families
- Protective Coatings
Other characteristics
- Brand
- Neoflon
- Features
- Abrasion Resistant, High Hardness
- Product Type
- Solventborne Coating
- Note
The above values in properties are typical and not guaranteed.
- Technology
- Ready-to-Use Products
- HIGHLIGHTS
Polyflon PTFE TC - 7400 grade is a solvent based PTFE coating.; Polyflon PTFE TC - 7400CR makes a clear coating layer displaying hardness and abrasion resistance and hardness.; It can be sintered at lower temperature (150 - 200℃).
- Ready to Use Product Features
- Abrasion Resistant
- High Hardness
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
Technical data
Table 1 of 2
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Contact Angle (Hexadecane, at 25°C) | 35 - 41 | Degree | Contact Angle Meter |
| Contact Angle (Water, at 25°C) | 92 - 96 | Degree | Contact Angle Meter |
| Film Appearance | Clear | — | — |
| Friction Coefficient (Bauden leben type, Steel ball 8mmφ, Linear velocity 0.27cm/s, Loading 1.0kg) | 0.04 – 0.08 | — | Bauden leben steel sheet |
| Maximum Temperature | 160 | °C | — |
| Pencil Hardness (at 25°C, after immersed in boiled water for 500hours) | 3 | H | Mitsubishi Uni |
| Solid Content | 35 | % | — |
| Specific Gravity | 0.98 | — | — |
| Viscosity (at 25℃) | 16 | sec | Ford Cup No.4 |
| Wear Resistance Sliding Abrasion (with SUS23B, 55.9kPa, 2.3m/s, 10 minutes) | 0.2 - 0.3 | mg/cm² | — |
| Wear Resistance Taber Abrasion (at 25°C, CS 17, 1kgf, 1000 rounds) | 25 - 35 | mg/1000 rounds | — |
Table 2 of 2
6 rows| Characteristic | Value |
|---|---|
| Chemical Resistance (for 16hours, at 25°C, Hydrochloric acid) | No change |
| Chemical Resistance (for 16hours, at 25°C, Methanol) | Not possible |
| Chemical Resistance (for 16hours, at 25°C, Nitric acid) | No change |
| Chemical Resistance (for 16hours, at 25°C, Sodium hydroxide) | Not possible (swelling) |
| Chemical Resistance (for 16hours, at 25°C, Sulfuric acid) | No change |
| Chemical Resistance (for 16hours, at 25°C, Xylene) | Swelling 1.0% |