Neoflon PFA TC-7405GN
- Chemical Family
- Fluoropolymers
Neoflon PFA TC-7405GN is identified as a solventborne coating, showcases features such as abrasion resistance and high hardness. Neoflon PFA TC-7405GN has a liquid physical form, this coating is well-suited for applications requiring robust protection.
Properties
- Physical Form
- Liquid
Product families
Ready-to-Use Products — Paints & Coatings
- Protective Coatings
Other characteristics
- Brand
- Neoflon
- Features
- Abrasion Resistant, High Hardness
- Product Type
- Solventborne Coating
- Note
The above values in properties are typical and not guaranteed.
- Technology
- Ready-to-Use Products
- HIGHLIGHTS
Polyflon PTFE TC - 7400 grade is a solvent based PTFE coating.; Polyflon PTFE TC - 7405GN makes a green coating layer displaying hardness and abrasion resistance and hardness.; It can be sintered at lower temperature (150 - 200℃).
- Ready to Use Product Features
- Abrasion Resistant
- High Hardness
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Contact Angle (Hexadecane, at 25°C) | 35 - 41 | Degree | Contact Angle Meter |
| Contact Angle (Water, at 25°C) | 92 - 96 | Degree | Contact Angle Meter |
| Film Appearance | Green | — | — |
| Friction Coefficient (Bauden leben type, Steel ball 8mmφ, Linear velocity 0.27cm/s, Loading 1.0kg) | 0.04 – 0.08 | — | Bauden leben steel sheet |
| Maximum Temperature | 160 | °C | — |
| Pencil Hardness (at 25°C, after immersed in boiled water for 500hours) | 3 | H | Mitsubishi Uni |
| Specific Gravity | 0.98 | — | — |
| Viscosity (at 25℃) | 16 | sec | Ford Cup No.4 |
| Wear Resistance Sliding Abrasion (with SUS23B, 55.9kPa, 2.3m/s, 10 minutes) | 0.2 - 0.3 | mg/cm² | — |
| Wear Resistance Taber Abrasion (at 25°C, CS 17, 1kgf, 1000 rounds) | 25 - 35 | mg/1000 rounds | — |
Table 2 of 2
6 rows| Characteristic | Value |
|---|---|
| Chemical Resistance (for 16hours, at 25°C, Hydrochloric acid) | No change |
| Chemical Resistance (for 16hours, at 25°C, Methanol) | Not possible |
| Chemical Resistance (for 16hours, at 25°C, Nitric acid) | No change |
| Chemical Resistance (for 16hours, at 25°C, Sodium hydroxide) | Not possible (swelling) |
| Chemical Resistance (for 16hours, at 25°C, Sulfuric acid) | No change |
| Chemical Resistance (for 16hours, at 25°C, Xylene) | Not possible |