DAI-EL G-701M
- Chemical Family
- Fluoropolymers
DAI-EL G-701M, available in solid form, features a good compression set and mechanical properties while being odorless. Designed for automotive applications, specifically in powertrains and UTH, it finds use in O rings. Soluble in lower ketones and esters, this product is suitable for compression molding processes.
Properties
- Physical Form
- Solid
Product families
Applications
- Powertrain & UTH
Product Families
- Fluoroelastomers
Other characteristics
- Brand
- DAI-EL
- Features
Good Compression Set, Good Mechanical Properties, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Processing Methods
- Compression Molding
- Note
*1 The above values are representative and not guaranteed.; *2 [Formula] DAI-EL G-701M: 100 phr, MT carbon black (N990): 20 phr, Calcium hydroxide: 6 phr, Magnesium Oxide (high-active): 3 phr [Curing condition] Press cure: 10min@170°C, Post cure: 24hrs@230°C.; *3 P-24 O-ring.
- Markets
- Automotive & Transportation
- Soluble In
- Lower ketones and esters
- Cure
- Chemical Cure
- Technology
- Elastomers
- Benefits
DAI-EL G-701M is a curing-incorporated copolymer of vinylidene fluoride and hexafluoropropylene.; It offers excellent compression set and mechanical properties and is suitable for seal material.; It is a standard type of bisphenol curable DAI-EL which is suitable for compression molding of simple shaped molding such as O-ring.
- Material Features
- Good Compression Set
- Good Mechanical Properties
- Odorless
- Packing Specification
- 20kg
- Plastics and Elastomers End Uses
- O Rings
- Safety Information
Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.. This product has been developed for industrial purpose and we shall not guarantee the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
- Plastics and Elastomers Processing Methods
- Compression Molding
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 200°C,70 hours, 25% Compression*³) | 15 | % | — |
| Elongation (at break) | 220 | % | ASTM D412 |
| Fluorine Content | 66 | mass% | — |
| Hardness (at 3 sec) | 67 | Shore A | ASTM D2240 |
| Hardness (at Peak) | 70 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10) | -18 | °C | ASTM D1329 |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 65 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 43 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.81 | — | ASTM D792 |
| Tensile Strength | 15.5 | MPa | ASTM D412 |
Table 2 of 2
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 5.4 | MPa | ASTM D412 |