DAI-EL G-372
- Chemical Family
- Fluoropolymers
DAI-EL G-372 is a versatile product available in sheet form, characterized by its odorless nature and excellent elongation properties. Designed for automotive and transportation applications, specifically in O rings and fuel entrance cover seals, it boasts a white color. With solubility in lower ketones and esters, this product caters to compression molding and transfer molding processing methods.
Properties
- Physical Form
- Sheets
Product families
- Exterior & Body
- Powertrain & UTH
Other characteristics
- Brand
- DAI-EL
- Color
- White
- End Uses
- Fuel Entrance Cover Seal, O Rings
- Features
- Good Elongation, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Tensile Strength
- 13.1 - 13.1 MPa
- Note
1 The above values are representative and not guaranteed. *2 [Formula] DAI-EL G-372: 100 phr, MT carbon black (N990): 20 phr, Calcium hydroxide: 6 phr, Magnesium Oxide (high-active): 3 phr, [Curing condition] Press cure: 10min@170°C, Oven cure: 24hrs@230°C. *3 P-24 O-ring.
- Markets
- Automotive & Transportation
- Soluble In
- Lower ketones and esters
- Technology
- Elastomers
- Benefits
DAI-EL G-372 is a cure-incorporated terpolymer of vinylidene fluoride and hexafluoropropylene which is suitable for transfer molding and compression molding.. It has excellent elongation at break.
- Product Families
- Elastomers — Parts & Shapes
- Material Features
- Good Elongation
- Odorless
- Packing Specification
- 20Kg
- Plastics and Elastomers End Uses
- Fuel Entrance Cover Seal
- O Rings
- Safety Information
Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.. This product has been developed for industrial purpose and we shall not guarantee the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
- Plastics and Elastomers Processing Methods
- Compression Molding
- Transfer Molding
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 200°C,70 hours, 25% Compression*³) | 25 | % | — |
| Elongation (at break) | 360 | % | ASTM D412 |
| Fluorine Content | 66 | mass% | — |
| Hardness (at 3 sec) | 61 | Shore A | ASTM D2240 |
| Hardness (at Peak) | 69 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10) | -18 | °C | ASTM D1329 |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 55 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀) (at 121°C) | 30 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.81 | — | ASTM D792 |
| Tensile Strength | 13.1 | MPa | ASTM D412 |
Table 2 of 2
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 2.5 | MPa | ASTM D412 |