DAI-EL G-755
- Chemical Family
- Fluoropolymers
DAI-EL G-755, in solid form, distinguishes itself with good processability and odorless characteristics. Suited for automotive and industrial applications, it excels in powertrains and equipment parts. Utilizing chemical cure and extrusion, this product offers reliable performance in components like fuel entrance cover seals and O rings.
Properties
- Physical Form
- Solid
Product families
Applications
- Powertrain & UTH
- Equipment & Parts
Product Families
- Fluoroelastomers
Other characteristics
- Brand
- DAI-EL
- Features
- Good Processability, Odorless
- Polymer Name
- Fluoroelastomer (FKM)
- Processing Methods
- Extrusion
- Note
*1 The above values are representative and not guaranteed.; *2 [Formula] DAI-EL G-755: 100 phr, SRF carbon black (N774): 13 phr, Calcium hydroxide: 6 phr, Magnesium Oxide (highactive): 3 phr, [Curing condition] Press cure: 10min at 170°C, Post cure: 24hrs at 230°C.; *3 Compression set: after post cure. The other items: after only press cure.; *4 P-24 O-ring.
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Cure
- Chemical Cure
- Technology
- Elastomers
- Material Features
- Good Processability
- Odorless
- HIGHLIGHTS
DAI-EL G-755 is a cure-incorporated copolymer of vinylidene fluoride and hexafluoropropylene.; It provides excellent extrusion processability.
- Packing Specification
- 20 Kg
- Plastics and Elastomers End Uses
- Fuel Entrance Cover Seal
- O Rings
- Safety Information
Be sure to read the Safety Data Sheet (SDS) and precautions on the label before using.. This product has been developed for industrial purposes and we shall not guarantee the safety if used for any other purposes. If it is going to be used for medical or food applications, please contact us in advance.
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Fluorine Content | 66 | mass% | — |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 45 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀)(at 121°C) | 25 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.81 | — | ASTM D792 |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 2.4 | MPa | ASTM D412 |
| Compression Set (70hours at 200°C, 25% Compression*⁴)*² | 22 | % | — |
| Elongation (at break)*² | 340 | % | ASTM D412 |
| Hardness (at 3 sec)*² | 61 | Shore A | ASTM D2240 |
| Hardness (at Peak)*² | 67 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10)*² | -18 | °C | ASTM D1329 |
| Tensile Strength*² | 14.1 | MPa | ASTM D412 |