DAI-EL G-801
- Chemical Family
- Fluoropolymers
DAI-EL G-801, in sheet form, features good mechanical properties, odorless characteristics, acid resistance, and steam resistance. Tailored for automotive and industrial applications, it excels in cooling and climate components. With chemical cure and compression molding as its preferred methods, this product ensures reliable performance in components like diaphragms, O rings, and turbocharger hoses.
Properties
- Physical Form
- Sheets
Product families
- Cooling & Climate
- Powertrain & UTH
- Equipment & Parts
Other characteristics
- Brand
- DAI-EL
- Color
- White
- End Uses
- Diaphragms, O Rings, Turbo Charger Hose
- Features
Acid Resistant, Good Mechanical Properties, Odorless, Steam Resistant
- Polymer Name
- Fluoroelastomer (FKM)
- Note
*1 The above values are representative and not guaranteed. *2 [Formula] DAI-EL G-801: 100 phr, MT carbon black (N990): 20 phr, Triallylisocyanurate (100% active): 4 phr, 2,5-dimethyl-2,5-di(t-butylperoxy)hexane (100% active): 1.5 phr, [Curing condition] Press cure: 10min at 160°C, Post cure: 4hrs at 180°C. *3 P-24 O-ring.
- Markets
- Automotive & Transportation
- Industrial
- Soluble In
- Lower ketones and esters
- Cure
- Chemical Cure
- Technology
- Elastomers
- Product Families
- Elastomers — Parts & Shapes
- Material Features
- Acid Resistant
- Good Mechanical Properties
- Odorless
- Steam Resistant
- HIGHLIGHTS
DAI-EL G-801 is a peroxide curable copolymer of vinylidene fluoride and hexafluoropropylene which is suitable for transfer and compression molding.. It provides superior mechanical properties and resistance to steam and acids compared with bisphenol curable products.
- Packing Specification
- 20 Kg
- Plastics and Elastomers End Uses
- Diaphragms
- O Rings
- Turbo Charger Hose
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
- Plastics and Elastomers Processing Methods
- Compression Molding
- Transfer Molding
Technical data
Table 1 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Fluorine Content | 66 | mass% | — |
| Mooney Viscosity (ML₁₊₁₀) (at 100°C) | 70 | MU | ASTM D1646 |
| Mooney Viscosity (ML₁₊₁₀)(at 121°C) | 37 | MU | ASTM D1646 |
| Specific Gravity (at 23°C) | 1.81 | — | ASTM D792 |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| 100% Tensile Stress*² | 1.8 | MPa | ASTM D412 |
| Compression Set (70hours at 200°C, 25% Compression*³)*² | 28 | % | — |
| Elongation (at break)*² | 440 | % | ASTM D412 |
| Hardness (at 3 sec)*² | 60 | Shore A | ASTM D2240 |
| Hardness (at Peak)*² | 65 | Shore A | ASTM D2240 |
| Low Temperature Retraction (TR10)*² | -19 | °C | ASTM D1329 |
| Tensile Strength*² | 21.8 | MPa | ASTM D412 |