Polyflon PTFE ED-3293SW1R
- Chemical Family
- Fluoropolymers
Polyflon PTFE ED-3293SW1R, a water-based PTFE topcoat, excels in providing both conductivity and non-stick properties. Categorized as a top coat and waterborne coating, it is specifically formulated for office automation equipment. Presented in a liquid form, it ensures easy application, making it a versatile and effective solution for enhancing performance in office automation equipment.
Properties
- Physical Form
- Liquid
Product families
- Top Coats
Other characteristics
- Brand
- Polyflon
- Features
- Conductive, Non Stick
- Product Type
- Top Coat, Waterborne Coating
- Top Coat
- Waterborne Coating
- Application Area
- Office Automation Equipments
- Note
- 1. The coating film was evaluated with a test piece below.
- Substrate
- Aluminum plate roughened with Tosa Emely Extra #80/#100=50/50
- Primer
- ED 1939D21R, approximately 10μm thick
- Topcoat
- Approximately 10 15μm thick
- 2. The above values in properties are typical and not guaranteed.
- Technology
- Ready-to-Use Products
- HIGHLIGHTS
Polyflon PTFE ED - 3200 grade is a water based PTFE topcoat.; Polyflon PTFE ED - 3293SW1R makes a grayish brown topcoat layer displaying conductivity and non stick property.; It is good for office automation equipments.
- Ready to Use Product Features
- Conductive
- Non Stick
- Safety Information
Be sure to read the notes on SDS and labels before use.. This product is intended for general industry, and therefore its adequacy and safety as a raw material for medical purposes cannot be guaranteed.
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| pH | 9 | — |
| Solid Content | 40 | mass% |
| Specific Gravity of Coating | approx. 1.3 - 1.4 | — |
| Viscosity | 260 | cP |
Table 2 of 3
1 row| Characteristic | Value |
|---|---|
| Film Appearance | Grayish brown |
Table 3 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Contact Angle (Hexadecane, at 25°C) | 45 - 55 | Degree | Contact Angle Meter |
| Contact Angle (Water, at 25°C) | 115 - 125 | Degree | Contact Angle Meter |
| Cross Cut Adhesion (Stripping with cellophane tape,10 times) | 100/100 | — | JIS K5400 8.5 |
| Pencil Hardness (at 200°C, Stripping hardness of base material) | 2B - B | — | JIS K6894 |
| Pencil Hardness (at 25°C, Stripping hardness of base material) | F - 2H | — | JIS K6894 |
| Surface Electrical Resistance (Measured a film which was made on a glass plate with Hiresta HT 450, 10~500V,10sec) | 1.0×10² - 9.9×10⁷ | Ω | — |
| Taber Abrasion (at 25°C, CS 17, 1kg, 1000 rounds) | 2 - 4 | mg/1000 rounds | — |