LNP™ STAT-KON™ Compound ZEL34XXC

Product families

Other characteristics

Brand

LNP™ STAT-KON™ Compound

Density

1230.0 - 1230.0 kg/m³

Polymer Name

PPO/PS Alloy

Flexural Modulus

8100.0 - 8100.0 MPa

Processing Methods

Injection Molding

Note

ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.; ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

Show in full

Markets

• Consumer Goods
• Electrical & Electronics
• Industrial

Flame Rating

UL 94 HB

Technology

Plastics

Fillers Included

• Carbon Fiber
• PTFE

Additives Included

• Lubricant (PTFE)
• Lubricant (Unspecified)
• Mold Release Agent

Material Features

• Electrically Conductive
• Friction Resistant
• Good Mold Release
• High Stiffness
• High Strength
• Light Weight
• Lubricated
• Wear Resistant

Country Availability

• Canada
• China (Mainland)
• Mexico
• USA

Certifications and Compliance

UL 94

Plastics and Elastomers End Uses

• Cash Dispenser (ATM)
• Electrical/Electronic Applications
• Home Appliances
• Industrial Applications
• Semiconductor Applications
• Vacuum Cleaners

Plastics and Elastomers Functions

Resin

Plastics and Elastomers Processing Methods

Injection Molding