LNP™ STAT-KON™ Compound DX03550

Chemical Family: Polycarbonate (PC)

LNP STAT-KON DX03550 compound is based on Polycarbonate (PC) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive.

Product families

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ STAT-KON™ Compound
Polymer Name: Polycarbonate (PC)
Fillers Included: Carbon Black, Carbon Powder
Carbon Black
Carbon Powder
Flexural Modulus: 2750.0 - 2750.0 MPa
Additives Included: Impact Modifier, Mold Release Agent
Impact Modifier
Mold Release Agent
Processing Methods: Extrusion, Injection Molding
Note: ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Electrical & Electronics
Industrial
Technology: Plastics
Material Features: Electrically Conductive
Good Mold Release
Impact Modified
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Carrier Tape
Electrical/Electronic Applications
Electronic Packaging
Industrial Applications
Semiconductor Applications
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Extrusion
Injection Molding

Technical data

Table 1 of 7

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield) ¹¹	58	MPa	ASTM D638
Tensile Strain (Break) ¹¹	20	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2750	MPa	ASTM D638
Flexural Stress ¹¹	96	MPa	ASTM D790
Flexural Modulus ¹¹	2750	MPa	ASTM D790

Table 2 of 7

1 row

Characteristic	Value	Unit	Method
Density ¹¹	1.25	g/cm³	ASTM D792

Table 3 of 7

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	129	°C	ASTM D648

Table 4 of 7

2 rows

Characteristic	Value	Unit	Method
Volume Resistivity ᵈ ¹¹	10000 - 10000000	Ω.cm	ASTM D257
Surface Resistivity ᵈ ¹¹	10000 - 10000000	Ω	ASTM D257

Table 5 of 7