LNP™ STAT-KON™ Compound QD000I

Chemical Family: Polyamides

SABIC's Specialties Business LNP STAT-KON QD000I compound is based on Nylon 6/10 resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, High Impact. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ STAT-KON™ Compound
Polymer Name: Polyamide 610 (PA 610)
Fillers Included: Carbon Black, Carbon Powder
Carbon Black
Carbon Powder
Flexural Modulus: 1720.0 - 1720.0 MPa
Additives Included: Impact Modifier
Processing Methods: Injection Molding
Note: ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Electrical & Electronics
Industrial
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: ESD Protection
Electrically Conductive
High Impact Resistance
Impact Modified
No Added PFAS
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Electrical/Electronic Applications
Industrial Applications
Semiconductor Applications
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

4 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	31	MPa	ASTM D638
Tensile Strain (Break) ¹¹	52.7	%	ASTM D638
Flexural Stress ¹¹	54	MPa	ASTM D790
Flexural Modulus ¹¹	1720	MPa	ASTM D790

Table 2 of 6

2 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.11	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.28	%	ASTM D570

Table 3 of 6

3 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	55	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000117	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000117	1/°C	ASTM E831

Table 4 of 6