LNP™ STAT-KON™ Compound PFD06
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP STAT-KON PFD06 compound is based on Nylon 6 resin containing conductive carbon powder and 30% glass fiber. Added features of this grade include: Electrically Conductive. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Equipment & Parts
- Industrial Automation
- Semiconductor Manufacturing
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ STAT-KON™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Carbon Black, Carbon Powder, Glass Fiber
- Carbon Black
- Carbon Powder
- Glass Fiber
- Flexural Modulus
- 11030.0 - 11030.0 MPa
- Additives Included
- Impact Modifier
- Processing Methods
- Injection Molding
- Note
ᵈ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье. НЕ смешивайте смолу NORYL GTX* с другими марками смол NORYL*. Эффективными материалами для продувки являются вторичный полистирол и акрил. Используйте диапазон температур, подходящий для конкретной продувочной смолы. Вторичное сырье также необходимо высушить. Максимум 25% вторичного сырья. Сушите при рекомендованных температурах и времени для оптимальных характеристик. Пересушивание может привести к потере физических свойств и/или появлению дефектов внешнего вида. Не превышайте рекомендованное основное время и температуру сушки:\n4-8 часов при 95°C (200°F), максимум 10 часов\n6-12 часов при 80°C (175°F), максимум 16 часов\n8-16 часов при 65°C (150°F), максимум 24 часа\nИЗБЕГАЙТЕ конвекционных сушильных шкафов. Уровень влажности в нагретом окружающем воздухе может превышать уровень влажности в самой смоле, что приводит к поглощению влаги, а не к сушке. Избегайте температуры расплава выше 300°C (575°F) и времени пребывания более 6-8 минут (может повлиять на свойства и/или внешний вид). Контроль температуры сопла помогает устранить подтекание и преждевременное затвердевание. Объемы впрыска, превышающие 50% объема цилиндра, могут привести к трудностям в обеспечении постоянного, однородного расплава пластмассы.; ᵍ Измерения выполнены на образцах для лабораторных испытаний. Фактическая усадка может отличаться от диапазона из-за различий в условиях переработки, оборудовании, геометрии детали и конструкции пресс-формы. Рекомендуется проводить исследования усадки в пресс-форме с помощью заменителя или предыдущей оснастки перед изготовлением оснастки для новой литой детали.; ⁷ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.; ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Electrically Conductive
- High Modulus
- High Stiffness
- Impact Modified
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Electrical Components
- Electrical/Electronic Applications
- Industrial Applications
- Semiconductor Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 159 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 2.3 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 11720 | MPa | ASTM D638 |
| Flexural Stress ¹¹ | 241 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 11030 | MPa | ASTM D790 |
Table 2 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.43 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.5 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.4 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.38 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.15 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.2 | % | ASTM D955 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.91 | % | ISO 62 |
Table 3 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 206 | °C | ASTM D648 |
Table 4 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ᵈ ¹¹ | 1000 | Ω.cm | ASTM D257 |
| Surface Resistivity ᵈ ¹¹ | 10 - 1000000 | Ω | ASTM D257 |
Table 5 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 907 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 106 | J/m | ASTM D256 |
Table 6 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 265 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 275 - 290 | °C |
| Middle - Zone 2 Temperature ⁷ | 265 - 275 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 260 | °C |
| Mold Temperature ⁷ | 80 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |