VINNAPAS® eco CA 55
- CASE Ingredients Functions
- Binder & Resin
VINNAPAS® eco CA 55 is an environmentally conscious product that helps conserve fossil resources. When purchasing this product, it is possible to replace up to 100% of the fossil-based raw materials used in its manufacturing with sustainably certified renewable feedstock. This substitution process follows the REDcert² mass balance approach, which is audited by TÜV Nord. The specific amount of fossil raw material replaced depends on the chosen product version and is specified in the REDcert² certificate.
Properties
- Physical Form
- Dispersion
Product families
Applications
- Consumer Goods — Footwear
- Textile & Footwear Adhesives
- Technical Fabrics
- Textile Manufacturing
Product Families
- Other Resins & Binders
Other characteristics
- Brand
- VINNAPAS® eco
- Glass Transition Temperature (Tg)
- 6.0 - 6.0 °C
- Markets
- Adhesives & Sealants
- Consumer Goods
- Industrial
- Shelf LIfe
- 6 Months
- Technology
- CASE Ingredients
- Storage Information
When the dispersion is stored in tanks, proper storage conditions must be maintained. The product has a shelf life of 6 months starting from the date of receipt if stored in the original, unopened containers at temperatures between 5 and 30°C.; Iron or galvanized iron containers and equipment are not recommended. Corrosion could result in discoloration of the dispersion or blends made from it in further processing. We therefore recommend the use of containers and equipment made of ceramic, rubberized or enameled materials, appropriately finished stainless steel, or plastic (rigid PVC, polyethylene or polyester resin).; As polymer dispersions may tend to superficial film formation, skins or lumps may be formed during storage or transportation. A filtration process is thus recommended prior to utilization of the product.; The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package.; Measures should also be taken to ensure cleanliness of the tanks and pipes. In unstirred tanks, a layer of preservativecontaining water should be sprayed onto the surface of the dispersion to prevent the formation of unwanted skin and possible attack by microorganisms.; The thickness of this water layer should be < 5 mm for low viscosity dispersions and up to 10–20 mm for high viscosity products. Proper procedures - periodic tank cleaning and sanitization - must be set up in order to prevent microbial attack. Contact your biocide representative/supplier for further plant hygiene recommendations. Measures should be taken to ensure that only clean air enters the tank when the dispersion is removed.; Finished products manufactured from polymer dispersions usually also require preservation. The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required.
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- ENCS (Japan)
- IECSC (China)
- NZIoC (New Zealand)
- PICCS (Phillipines)
- TCSI (Taiwan)
- TSCA (USA)
- Country Availability
- Albania
- Andorra
- Austria
- Belgium
- Bosnia and Herzegovina
- Bulgaria
- Croatia
- Cyprus
- Certifications and Compliance
- REACH (Europe)
Technical data
Table 1 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (at 20°C) | approx. 1.08 | g/cm³ | ISO 2811 |
| Filler and Pigment Compatibility | Excellent | — | Specific method |
| Glass Transition Temperature | approx. 6 | °C | Specific method |
| Minimum Film Forming Temperature | 0 | °C | DIN ISO 2115 |
| Predominant Particle Size | 0.5 - 1.0 | µm | Specific method |
Table 2 of 2
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dynamic Viscosity (at 23°C) | 1000 - 3000 | mPa·s | DIN EN ISO 2555 |
| pH | 5.0 - 7.0 | — | DIN/ISO 976 |
| Solids Content | 61 - 63 | % | DIN EN ISO 3251 |