VINNAPAS® 536 ED
- Chemical Family
- Vinyl Acetate Ethylene (VAE) Copolymer
VINNAPAS® 536 ED is a versatile polymer dispersion based on vinyl acetate and ethylene with a high solid content. It is produced without the use of organic solvents, plasticizers, or formaldehyde donors. The residual monomer content is below 1000 ppm. The dispersion is characterized by high bonding strength combined with increased flexural strength and good compatibility with inorganic fillers like CaCO3.
Properties
- Physical Form
- Dispersion
Other characteristics
- Brand
- VINNAPAS
- Features
Excellent Adhesion, Good Compatibility, Improved Flexural Strength, Water Resistance
- Functions
- Binder, Binder & Resin, Filler
- Markets
- Building & Construction
- Paints & Coatings
- Printing & Packaging
- Shelf LIfe
- 9 Months
- Coating Type
- Primer
- Skim Coat
- Technology
- CASE Ingredients
- Industrial Additives & Materials
- Packaging Type
- Drums
- Labeling Claims
- Plasticizer-free
- Application Details
VINNAPAS® 536 ED offers several advantages in a wide range of building chemical and construction applications. It exhibits a high compatibility towards cement and its influence on cement setting is marginal. The dispersion is characterized by a high bonding strength combined with increased flexural strength and by good compatibility with inorganic fillers like CaCO3. VINNAPAS® 536 ED is compatible with other dispersions (such as styrene/acrylic and pure acrylic dispersions). We recommend VINNAPAS® 536 ED for use in applications such as waterproofing membranes (WPM), bonding agents, tile adhesives, putties and joint compounds, primer and bonding agents, cement admixtures and for skim coats. For typical application fields of VINNAPAS® 536 ED you can refer to the section "application".
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (at 20°C) | approx. 1.07 | g/cm³ | Specific method |
| Filler and Pigment Compatibility | Excellent | — | Specific method |
| Glass Transition Temperature | 4 - 10 | °C | Specific method |
| Minimum Film Forming Temperature | 0 | °C | Specific method |
| Predominant Particle Size | 0.5 - 1.0 | µm | Specific method |
| Residual Monomer (Vinyl acetate) | max. 0.1 | % | Gas Chromatography |
Table 2 of 2
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dynamic Viscosity (at 25°C) | 200 - 800 | mPa·s | Specific method |
| pH | 6.0 - 7.5 | — | Specific method |
| Solids Content | 62.5 - 64.0 | % | Specific method |