ELASTOSIL® LR 6240 A/B
- Chemical Family
- Silicones
ELASTOSIL® LR 6240 A/B is a solvent-free, free-flowing, addition-curing two-component silicone rubber for textile coatings (e.g. electrical sleevings). This low-viscosity compound is used to produce flexible textile coatings. It is especially suitable for the manufacture of conveyor belts and electrical insulation tubing.
Properties
- Physical Form
- Liquid
Product families
Applications
Industrial — Leather & Textiles
- Textile Manufacturing
Product Families
CASE Ingredients — Resins & Binders
- Other Resins & Binders
Other characteristics
- Brand
- ELASTOSIL® LR
- End Uses
- 2K (2 component) Coating
- Features
Excellent Flow, High Modulus, Improved Flexibility, Low Viscosity
- Compatible Substrates & Surfaces
- Textiles
- Note
Cure conditions: mixture of LR 6240 A/B in ratio 1 : 1, 5 min / 165°C for cured properties.
- Markets
- Industrial
- Properties
- High flexibility and resilience
- High modulus
- Coating Type
- 2K (2 component) Coating
- Technology
- CASE Ingredients
- Packaging Type
- Drums
- Pails
- Labeling Claims
- Solvent-free
- Storage Information
Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.
Technical data
Table 1 of 3
1 row| Characteristic | Value | Unit |
|---|---|---|
| Pot Life (at 23°C) | 3 | Days |
Table 2 of 3
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | DIN EN ISO 1183-1 A |
| Dielectric Strength (1mm sheet) | 19 | kV/mm | IEC 60243-1 |
| Dissipation Factor (tan δ, at 50Hz) | 140 × 10⁻⁴ | — | IEC 62631-2-1 |
| Elongation (at break) | 290 | % | ISO 37 Type 1 |
| Oxygen Index (LOI) | 26 | % | ASTM D 2863 |
| Permittivity (at 50Hz) | 2.9 | — | IEC 62631-2-1 |
| Shore Hardness A | 30 | — | DIN ISO 48-4 |
| Tear Strength | 4.9 | N/mm | ASTM D 624 B |
| Tensile Strength | 1.7 | N/mm² | ISO 37 Type 1 |
| Volume Resistivity | 5 x 10¹⁴ | Ohm-cm | IEC 62631-3-1 |
Table 3 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dynamic Viscosity (at 2.5 rpm, Component A) | 25000 | mPa·s | Brookfield |
| Dynamic Viscosity (at 2.5 rpm, Component B) | 25000 | mPa·s | Brookfield |