ELASTOSIL® LR 3852/50 A/B
- Chemical Family
- Silicones
ELASTOSIL® LR 3852/50 A/B is a low-oil-bleeding liquid silicone rubber of the ELASTOSIL® LR 3852 series. It is a paste-like, easily pigmentable, two-component product with short curing times and very good demoldability (high hot tear resistance). Shortly after curing, a thin oil film with lubricating properties forms on the surface. The vulcanizates are opaque, have very good mechanical and electrical properties, excellent cut resistance, and a low compression set without post-cure.
Properties
- Physical Form
- Paste
Product families
- Silicone Elastomers
Other characteristics
- Brand
- ELASTOSIL® LR
- End Uses
Automobile Door Seals, Automotive Connector Seals, Batteries, Cables
- Features
Cost Effective, Cut Through Resistant, Enhanced Tear Resistant, Excellent Lubricity, Excellent Opacity, Fast Curing, Good Electrical Properties, Good Mechanical Properties, Good Mold Release, Heat Stabilized, High Bleed Resistant, Low Compression Set, Low VOC, Low Volatility, Oil Resistant, Pigmentable
- Polymer Name
- Liquid Silicone Rubber (LSR)
- Tear Strength
- 40.0 - 40.0 kN/m
- Note
- Cure conditions : 5 min / 165°C in press.
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Industrial
- Properties
This product can be used within a temperature range of - 55°C to + 210°C. The addition of heat stabilizers at service temperatures of more than 180°C is recommended.
- Technology
- Elastomers
- Packaging Type
- Drums
- Pails
- Specific Features
- Fast curing
- Low compression set without post-cure
- Oil bleeding
- Reduced volatile content
- Additives Included
- Heat Stabilizer
- Material Features
- Cost Effective
- Cut Through Resistant
- Enhanced Tear Resistant
- Excellent Lubricity
- Excellent Opacity
- Fast Curing
- Good Electrical Properties
- Good Mechanical Properties
- Storage Information
Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 22 hours, 175°C) | 15 | % | DIN ISO 815-1 type B method A |
| Density | 1.13 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break) | 560 | % | ISO 37 Type 1 |
| Fluid Content | approx. 2.5 | % | — |
| Shore Hardness A | 47 | — | DIN ISO 48-4 |
| Tear Strength | 40 | N/mm | ASTM D 624 B |
| Tensile Strength | 9 | N/mm² | ISO 37 Type 1 |
Table 2 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dynamic Viscosity (Shear rate 1 s⁻¹) | 2300000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (Shear rate 10 s⁻¹) | 600000 | mPa·s | DIN EN ISO 3219 |