ELASTOSIL® LR 3170/40 A/B
- Chemical Family
- Silicones
ELASTOSIL® LR 3170/40 A/B is a self-adhesive liquid silicone rubber of the ELASTOSIL® LR 3170 series. It is a paste-like, low-inflammable, two-component compound with an extremely short curing time. The vulcanizates of this product are noted for their excellent mechanical and electrical properties.
Properties
- Physical Form
- Paste
Product families
- Silicone Elastomers
Other characteristics
- Brand
- ELASTOSIL® LR
- End Uses
- Automobile Door Seals
- Features
Cost Effective, Fast Curing, Flame Retardant, Good Electrical Properties, Good Mechanical Properties, Heat Resistance, Low Flammability, Low VOC, Low Volatility
- Polymer Name
- Liquid Silicone Rubber (LSR)
- Tear Strength
- 23.0 - 23.0 kN/m
- Processing Methods
- Injection Molding, Liquid Injection Molding
- Note
- Cure conditions : 5 min / 165°C in press.
- Markets
- Automotive & Transportation
- Industrial
- Properties
ELASTOSIL® LR 3271 series are primerless, selfbonding grades that adhere to various plastic substrates (e.g. PET, PBT) and metals, but not in the mold. The bonding is improved by a subsequent heat treatment process (e.g. four hours at 100°C). Because of the individual surface properties each substrate must be tested before mass production. If necessary one has to check the development of adhesive properties over time and/or in an environment relevant to the application.
- Flame Rating
- UL 94 V0
- Technology
- Elastomers
- Packaging Type
- Drums
- Pails
- Specific Features
- Food-contact
- Hot water resistant
- Reduced volatile contentSelf-adhesive
- Material Features
- Cost Effective
- Fast Curing
- Flame Retardant
- Good Electrical Properties
- Good Mechanical Properties
- Heat Resistance
- Low Flammability
- Low VOC
- Storage Information
Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.
Technical data
Table 1 of 2
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 22 hours, 125°C) | 29 | % | DIN ISO 815-1 type B method A |
| Density | 1.12 | g/cm³ | DIN EN ISO 1183-1 A |
| Dielectric Strength (1mm sheet) | 29 | kV/mm | IEC 60243-1 |
| Elongation (at break) | 590 | % | ISO 37 Type 1 |
| Loss on Ignition | 35 | % | EN ISO 4589-2 / ASTM D2863 |
| Shore Hardness A | 45 | — | DIN ISO 48-4 |
| Tear Strength | 23 | N/mm | ASTM D 624 B |
| Tensile Strength | 9.8 | N/mm² | ISO 37 Type 1 |
| Volume Resistivity | 5 x 10¹⁵ | Ohm-cm | IEC 62631-3-1 |
Table 2 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dynamic Viscosity (Shear rate 1 s⁻¹) | 1600000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (Shear rate 10 s⁻¹) | 400000 | mPa·s | DIN EN ISO 3219 |