ELASTOSIL® LR 3022/60 A/B
- Chemical Family
- Silicones
ELASTOSIL® LR 3022/60 A/B is a liquid silicone rubber. It is a paste-like, easily pigmentable, two-component compound with short curing times and excellent coolant resistance. The vulcanizates of this product are opaque with average mechanical properties. However, they are highly recognized for their ultra-low compression sets after post-curing.
Properties
- Physical Form
- Paste
Product families
- Silicone Elastomers
Other characteristics
- Brand
- ELASTOSIL® LR
- End Uses
- Automobile Door Seals, Gaskets, Radiator Seals
- Features
Coolant Resistant, Cost Effective, Fast Curing, Good Mechanical Properties, Low Compression Set, Low VOC, Low Volatility, Pigmentable
- Polymer Name
- Liquid Silicone Rubber (LSR)
- Tear Strength
- 14.0 - 14.0 kN/m
- Note
- Cure conditions
- 5 min / 165°C in press, post-cured 4 h / 200°C.
- Coolant resistance
- After immersion 1000 h / 125°C in coolant / distilled water 50:50.
- Color
- Opaque
- Markets
- Automotive & Transportation
- Industrial
- Properties
ELASTOSIL® LR 3022/60 offers excellent coolant resistance, especially extremely low compression set in contact with coolant fluids.
- Technology
- Elastomers
- Packaging Type
- Drums
- Pails
- Specific Features
- Coolant resistant
- Reduced volatile content
- Ultra-low compression set
- Material Features
- Coolant Resistant
- Cost Effective
- Fast Curing
- Good Mechanical Properties
- Low Compression Set
- Low VOC
- Low Volatility
- Pigmentable
- Storage Information
Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- ENCS (Japan)
- IECSC (China)
- PICCS (Phillipines)
- TCSI (Taiwan)
- TSCA (USA)
Technical data
Table 1 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (Glysantin® G40 / distilled water 50:50) | 42 | % | DIN ISO 815-1 |
| Compression Set (Glysantin® G48 / distilled water 50:50) | 48 | % | DIN ISO 815-1 |
| Elongation (at break, Glysantin® G40 / distilled water 50:50) | 230 | % | ISO 37 |
| Elongation (at break, Glysantin® G48 / distilled water 50:50) | 220 | % | ISO 37 |
| Shore Hardness A (Glysantin® G40 / distilled water 50:50) | 61 | — | DIN ISO 48-4 |
| Tensile Strength (Glysantin® G40 / distilled water 50:50) | 5.1 | N/mm² | ISO 37 |
| Tensile Strength (Glysantin® G48 / distilled water 50:50) | 5.1 | N/mm² | ISO 37 |
Table 2 of 3
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 22 hours, 175°C) | 7 | % | DIN ISO 815-1 type B method A |
| Density | 1.11 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break) | 270 | % | ISO 37 Type 1 |
| Shore Hardness A | 61 | — | DIN ISO 48-4 |
| Tear Strength | 14 | N/mm | ASTM D 624 B |
| Tensile Strength | 6.1 | N/mm² | ISO 37 Type 1 |
Table 3 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dynamic Viscosity (Shear rate 1 s⁻¹) | 1000000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (Shear rate 10 s⁻¹) | 220000 | mPa·s | DIN EN ISO 3219 |