ELASTOSIL® LR 3003/03 A/B
- Chemical Family
- Silicones
ELASTOSIL® LR 3003/03 A/B is a liquid silicone rubber of the ELASTOSIL® LR 3003 series. It is a paste-like, easily pigmentable, two-component compound with short curing times. The vulcanizates of this product are renowned for their high transparency as well as their exceptional mechanical and electrical properties.
Properties
- Physical Form
- Paste
Product families
- Silicone Elastomers
Other characteristics
- Brand
- ELASTOSIL® LR
- End Uses
- Automobile Door Seals, General Purpose
- Features
Cost Effective, Excellent Transparency Properties, Fast Curing, General Purpose, Good Electrical Properties, Good Mechanical Properties, Heat Stabilized, Low VOC, Low Volatility, Pigmentable
- Polymer Name
- Liquid Silicone Rubber (LSR)
- Tear Strength
- 3.0 - 3.0 kN/m
- Processing Methods
- Injection Molding
- Note
Cure conditions: 5 min / 165°C in press, post-cured 4 h / 200°C.
- Markets
- Automotive & Transportation
- Industrial
- Properties
This product can be used within a temperature range of - 55 °C to + 210 °C. The addition of heat stabilizers at service temperatures of more than 180°C is recommended.
- Technology
- Elastomers
- Packaging Type
- Drums
- Pails
- Specific Features
- General purpose
- Reduced volatile content
- Additives Included
- Heat Stabilizer
- Material Features
- Cost Effective
- Excellent Transparency Properties
- Fast Curing
- General Purpose
- Good Electrical Properties
- Good Mechanical Properties
- Heat Stabilized
- Low VOC
- Storage Information
Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- ENCS (Japan)
- IECSC (China)
- PICCS (Phillipines)
- TCSI (Taiwan)
- TSCA (USA)
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 22 hours, 175°C) | 16 | % | DIN ISO 815-1 type B method A |
| Density | 1.01 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break) | 700 | % | ISO 37 Type 1 |
| Shore Hardness A | 3 | — | DIN ISO 48-4 |
| Tear Strength | 3 | N/mm | ASTM D 624 B |
| Tensile Strength | 1.3 | N/mm² | ISO 37 Type 1 |
Table 2 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dynamic Viscosity (Shear rate 1 s⁻¹) | 30000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (Shear rate 10 s⁻¹) | 25000 | mPa·s | DIN EN ISO 3219 |