SuperOhm® 3753
- Chemical Family
- Ethylene-Propylene Copolymers (EPR)
Off-white colorable, flame retardant, low voltage composition in pellet form, EPDM-rubber based and containing peroxide curing agent, ready for extrusion in a conventional CV line.
Properties
- Physical Form
- Pellets
- Solid
Product families
- EP Rubbers (EPDM)
Other characteristics
- Brand
- SuperOhm
- Density
- 1200.0 - 1240.0 kg/m³
- Polymer Name
- Ethylene Propylene Copolymer
- Processing Methods
- Extrusion
- Markets
- Electrical & Electronics
- Industrial
- Storage
SUPEROHM®3753 containers should be stored at temperatures below 50C (120F) in a dry area to avoid massing of pellets. Product is recommended to be used within 12 months.
- PACKAGING
- 1,600 pounds (726 Kg) per sealed box.
- Cure
- Chemical Cure
- Technology
- Elastomers
- Certification
Certified Test Results including physical test data are included with each shipment.
- Packaging Type
- Boxes
- Specifications
When extruded and cured consistent with standard safe wire and cable industry practices, cable insulated with SUPEROHM®3753 EPR insulation will comply with the requirements as specified in the following standards: UL 44 (14 AWG) ICEA S-68-516 NEMA Pub. No. WC-70, WC-71, WC-74 ANSI / ICEA S-94-649-2000 Class I, II, III IEC Publication 60502 UL 1072 for type MV-90, MV-105
- Labeling Claims
- Halogen-free
- Lead-free
Technical data
Table 1 of 3
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation | 300 | % |
| Final Set (ECC test method) | 4.2 | % |
| Hot Creep (at 150°C) | 7.3 | % |
| Specific Gravity | 1.2 - 1.24 | — |
| Tensile Strength | 1500 | psi |
Table 2 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Retained Elongation (7 days in 121°C air oven) | 87 | % |
| Retained Elongation (7 days in 136°C air oven) | 92 | % |
| Retained Tensile (7 days in 121°C air oven) | 99 | % |
| Retained Tensile (7 days in 136°C air oven) | 103 | % |
Table 3 of 3
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Volume Resistivity | 1.0 X 10^16 | Ohm-cm |
| Dielectric Constant | 3.45 | — |