SuperOhm® 2502
- Chemical Family
- Ethylene-Propylene Copolymers (EPR)
Off-white colorable, flame retardant, low voltage composition in pellet form, EPDM-rubber based and containing peroxide curing agent, ready for extrusion in a conventional CV line.
Properties
- Physical Form
- Pellets
- Solid
Product families
- EP Rubbers (EPDM)
Other characteristics
- Brand
- SuperOhm
- Density
- 1120.0 - 1160.0 kg/m³
- Polymer Name
- Ethylene Propylene Copolymer
- Processing Methods
- Extrusion
- Color
- White
- Markets
- Electrical & Electronics
- Industrial
- Storage
SUPEROHM® 2502 containers should be stored at temperatures below 50°C (120°F) in a dry area to avoid massing of pellets. Product is recommended to be used within 12 months.
- Handling
To ensure health and safety, Material Safety Data Sheets (MSDS) are available and should be consulted prior to use.
- PACKAGING
To ensure health and safety, Material Safety Data Sheets (MSDS) are available and should be consulted prior to use.
- Cure
- Chemical Cure
- Technology
- Elastomers
- Certification
Certified Test Results including physical test data are included with each shipment.
- Packaging Type
- Boxes
- Specifications
When extruded and cured consistent with standard safe wire and cable industry practices, cable insulated with SUPEROHM® 2502 EPR insulation will comply with the requirements as specified in the following standards: UL 44 (14 AWG) RHH, RHW, RHW-2 USE, USE-2 SIS
- Labeling Claims
- Halogen-free
- Lead-free
Technical data
Table 1 of 3
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation | 400 | % |
| Specific Gravity | 1.12 - 1.16 | — |
| Tensile Strength | 1600 | psi |
Table 2 of 3
8 rows| Characteristic | Value | Unit |
|---|---|---|
| Retained Elongation (7 days in 136°C air oven) | 98 | % |
| Retained Elongation (7 Days in 160°C Air Oven) | 90 | % |
| Retained Elongation (7 Days in 170°C Air Oven) | 91 | % |
| Retained Elongation (7 Days in 180°C Air Oven) | 90 | % |
| Retained Tensile (7 Days in 136°C Air Oven) | 97 | % |
| Retained Tensile (7 Days in 160°C Air Oven) | 104 | % |
| Retained Tensile (7 Days in 170°C Air Oven) | 106 | % |
| Retained Tensile (7 Days in 180°C Air Oven) | 98 | % |
Table 3 of 3
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Cold Blend (at -25°C for 4hrs) | No cracks | — |
| Deformation (60 Minutes at 120°C) | 5 | % |
| Dielectric Constant | 2.9 | — |
| Dielectric Strength | 800 | V/mil |
| I.R. Constant (at 15.6ºC) | 70000 | MΩ-1000ft |
| Volume Resistivity | 1.0 X 10^16 | Ohm-cm |