SuperOhm® 2560
- Chemical Family
- Ethylene-Propylene Copolymers (EPR)
Superohm® 2560 is an oil and solvent resistant off-white colorable polymeric composition in pellet form, based on EPDM rubber containing peroxide curing agent, ready for extrusion in a conventional CV or dry cure extrusion line. Cables jacketed with this compound are recognized for balanced properties including excellent heat and deformation resistance at high temperatures, oil resistance, and superior mechanical properties and is suitable for operation up to 450F (230C) in appropriate cable construction when extruded and cured consistent with industry standards.
Properties
- Physical Form
- Pellets
- Solid
Product families
- EP Rubbers (EPDM)
Other characteristics
- Brand
- SuperOhm
- Density
- 1170.0 - 1210.0 kg/m³
- Polymer Name
- Ethylene Propylene Copolymer
- Processing Methods
- Extrusion
- Markets
- Electrical & Electronics
- Industrial
- Storage
SUPEROHM® 2560 containers should be stored at temperatures below 50°C (120°F) in a dry area to avoid massing of pellets. Product is recommended to be used within 12 months.
- Handling
To ensure health and safety, Material Safety Data Sheets (MSDS) are available and should be consulted prior to use.
- PACKAGING
To ensure health and safety, Material Safety Data Sheets (MSDS) are available and should be consulted prior to use.
- Cure
- Chemical Cure
- Technology
- Elastomers
- Certification
Certified Test Results including physical test data are included with each shipment.
- Packaging Type
- Boxes
- Labeling Claims
- Halogen-free
- Lead-free
- Quality Standards
- ISO 6722 Class A
- SAE J1128
- Material Features
- Cost Effective
- Crosslinkable
- Good Colorability
- Good Electrical Properties
- Good Mechanical Properties
- Good Solvent Resistance
- Heat Resistance
- High Performance
Technical data
Table 1 of 2
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation | 175 | % |
| Specific Gravity | 1.17 - 1.21 | — |
| Tensile Strength | 1900 | psi |
Table 2 of 2
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Retained Elongation (7 Days in 121°C Air Oven) | 88 | % |
| Retained Elongation (902 Oil Immersion - 168 Hours at 150°C) | 58 | % |
| Retained Tensile (7 Days in 121°C Air Oven) | 110 | % |
| Retained Tensile (902 Oil Immersion 168 Hours at 150°C) | 81 | % |