Excelene 1000
- Chemical Family
- Polyethylene Cross-Linked (PEX)PolyethylenesPolyolefins
Excelene 1000 are crosslinkable elastomeric polyolefin compounds designed for high temperature applications requiring a balance of mechanical properties, electrical properties, thermal stability, and performance.
Properties
- Physical Form
- Pellets
- Solid
Product families
- Other Thermoset Elastomers
Other characteristics
- Brand
- Excelene
- End Uses
Cable Jacketing, Cables, High Voltage Insulation, Industrial Cable Insulation, Industrial Cable Jacketing, Medium Voltage Insulation, Power Cable Jacketing, Underground Power Cable, Wires
- Features
Cost Effective, Crosslinkable, Good Electrical Properties, High Performance
- Polymer Name
- Crosslinked Polyethylene (XLPE / PEX)
- Strain at Break
- 420.0 - 420.0 %
- Processing Methods
- Extrusion
- Type
- MV/HV Filled XLPE Insulation
- Color
- White
- Markets
- Electrical & Electronics
- Industrial
- Storage
EXCELENE 1000 containers should be stored at temperatures below 50C (120F) in a dry area to avoid massing of pellets. Product is recommended to be used within 12 months.
- Handling
To ensure health and safety, Material Safety Data Sheets (MSDS) are available and should be consulted prior to use.
- PACKAGING
- 1,500 pounds (681 Kg) per box.
- Cure
- Chemical Cure
- Technology
- Elastomers
- Certification
Certified Test Results including physical test data are included with each shipment.
- Packaging Type
- Boxes
- Specifications
When extruded and cured consistent with standard safe wire and cable industry practices, cable insulated with EXCELENE 1000 XLPE insulation will meet or exceed the requirements as specified in the following standards: ASTM D-2802 and D-2770 ICEA S-68-516 IEC Publication 60502 AEIC CS8-00 UL 1072 for type MV-90
- Labeling Claims
- Halogen-free
- Fillers Included
- Mineral
- Quality Standards
- ISO 6722 Class A
- SAE J1128
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity | 1.13 | — |
| Tensile Strength | 2500 | psi |
| UL 44 Crush Test | 1800 | lbs. |
| Ultimate Elongation | 420 | % |
Table 2 of 3
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Heat Distortion (at 121°C 500gm) | 5 | % |
| Retained Elongation (7 days in 121°C air oven) | 95 | % |
| Retained Elongation (7 days in 136°C air oven) | 75 | % |
| Retained Elongation (7 days in 158°C air oven) | 90 | % |
| Retained Tensile (7 days in 121°C air oven) | 100 | % |
| Retained Tensile (7 days in 136°C air oven) | 100 | % |
| Retained Tensile (7 days in 158°C air oven) | 100 | % |
Table 3 of 3
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Dielectric Strength | 1400 | V/mil |
| I.R. Constant (at 15.6ºC) | 80000 | MΩ-1000ft |