SuperOhm® 2565
- Chemical Family
- Ethylene-Propylene Copolymers (EPR)
Superohm® 2565 is an oil and solvent resistant off-white colorable polymeric composition in pellet form, based on EPDM rubber containing peroxide curing agent, ready for extrusion in a conventional CV or dry cure extrusion line. It is formulated to obtain balanced performance characteristics with excellent electrical properties suitable for operation up to 450F (230C) and 25 kV in appropriate cable construction when extruded and cured consistent with industry standards.
Properties
- Physical Form
- Pellets
- Solid
Product families
- EP Rubbers (EPDM)
Other characteristics
- Brand
- SuperOhm
- Density
- 1130.0 - 1170.0 kg/m³
- Polymer Name
- Ethylene Propylene Copolymer
- Processing Methods
- Extrusion
- Color
- White
- Markets
- Electrical & Electronics
- Industrial
- Storage
SUPEROHM® 2565 containers should be stored at temperatures below 50°C (120°F) in a dry area to avoid massing of pellets. Product is recommended to be used within 12 months.
- Handling
To ensure health and safety, Material Safety Data Sheets (MSDS) are available and should be consulted prior to use.
- PACKAGING
To ensure health and safety, Material Safety Data Sheets (MSDS) are available and should be consulted prior to use.
- Cure
- Chemical Cure
- Technology
- Elastomers
- Certification
Certified Test Results including physical test data are included with each shipment.
- Packaging Type
- Boxes
- Specifications
When extruded and cured consistent with standard safe wire and cable industry practices, cable insulated with SUPEROHM® 2565 EPR insulation will comply with the requirements as specified in the following standards: UL 44 (14 AWG) RHH, RHW, RHW-2 USE, USE-2 SIS
- Labeling Claims
- Halogen-free
- Lead-free
Technical data
Table 1 of 3
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation | 140 | % |
| Specific Gravity | 1.13 - 1.17 | — |
| Tensile Strength | 2200 | psi |
Table 2 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Retained Elongation (902 Oil Immersion - 168 Hours at 150°C) | 61 | % |
| Retained Elongation (902 Oil Immersion - 18 Hours at 121°C) | 60 | % |
| Retained Tensile (902 Oil Immersion 168 Hours at 150°C) | 68 | % |
| Retained Tensile (902 Oil Immersion 18 Hours at 121°C) | 70 | % |
Table 3 of 3
1 row| Characteristic | Value |
|---|---|
| Dielectric Constant | 2.65 |