SuperOhm® 3455
- Chemical Family
- Ethylene-Propylene Copolymers (EPR)
SuperOhm® 3455 peroxide crosslinkable EPR compounds are designed for high temperature stability and superior electrical performance.
Properties
- Physical Form
- Pellets
- Solid
Product families
Elastomers — Thermoset Elastomers
- EP Rubbers (EPDM)
Other characteristics
- Brand
- SuperOhm
- Density
- 1500.0 - 1500.0 kg/m³
- Polymer Name
- Ethylene Propylene Copolymer
- Additives Included
- Flame Retardant
- Processing Methods
- Extrusion
- Type
- Low Voltage FR EPR Insulation
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Industrial
- Storage
SUPEROHM® 3455 containers should be stored at temperatures below 50 °C (120°F ) in a dry area to avoid massing of pellets. Product is recommended to be used within 12 Months.
- Handling
To ensure health and safety, Material Safety Data Sheets (MSDS) are available and should be consulted prior to use.
- PACKAGING
- 1,750 pounds (794 Kg) per box.
- Cure
- Chemical Cure
- Technology
- Elastomers
- Certification
Certified Test Results including physical test data are included with each shipment.
- Packaging Type
- Boxes
- Specifications
When extruded and cured consistent with standard safe wire and cable practices, cables manufactured with SUPEROHM® 3455 are designed to be recognized for IEEE P1580 MIL C-24643
- Labeling Claims
- Halogen-free
- Lead-free
Technical data
Table 1 of 3
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation | 170 | % |
| Specific Gravity | 1.5 | — |
| Tensile Strength | 1750 | psi |
Table 2 of 3
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Acid Gas Equivalent | 0.01 | — |
| Horizontal Flame Test | Pass | — |
| Retained Elongation (902 Oil Immersion - 60 Days at 75°C) | 80 | % |
| Retained Elongation (7 Days in 136°C Air Oven) | 100 | % |
| Retained Elongation (7 Days in 158°C Air Oven) | 95 | % |
| Retained Elongation (7 Days in 180°C Air Oven) | 40 | % |
| Retained Elongation (902 Oil Immersion - 96 Hours at 100°C) | 85 | % |
| Retained Tensile (7 Days in 136°C Air Oven) | 125 | % |
| Retained Tensile (7 Days in 158°C Air Oven) | 135 | % |
| Retained Tensile (7 Days in 180°C Air Oven) | 110 | % |
| Retained Tensile (902 Oil Immersion 60 Days at 75°C) | 110 | % |
| Retained Tensile (902 Oil Immersion 96 hours at 100°C) | 100 | % |
Table 3 of 3
2 rows| Characteristic | Value | Unit |
|---|---|---|
| I.R. Constant (at 15.6ºC) | 2600 | MΩ-1000ft |
| Volume Resistivity | 1.0 E+15 | Ohm-cm |