AquaGraft® 1-6010
Aquagraft® 1-6010 is Polyethylene moisture curable system that allows customers to crosslink polymer systems without investing in expensive curing processes.
Properties
- Physical Form
- Pellets
- Solid
Other characteristics
- Brand
- AquaGraft
- End Uses
Appliance Wire Jacketing, Appliances, Automotive Components, Building Wire Insulation, Cables, Communication Cable Jacketing, Low Voltage Insulation, Power Cable Jacketing, Wires
- Features
Cost Effective, Crosslinkable, Flame Retardant, Good Electrical Properties, High Performance
- Polymer Name
- Crosslinked Polyethylene (XLPE / PEX)
- Strain at Break
- 450.0 - 450.0 %
- Processing Methods
- Extrusion
- Type
- Low Voltage FR Polyolefin Insulation
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Storage
A high level of care in storage to minimize exposure to moisture is recommended to ensure that there is no pre-cure or gelling of the PEMC-1 grafted polymer. Component containers should be stored at temperatures below 50C (120F) in a dry area for not more than 6 months. Once opened, PEMC-1 must be used immediately to avoid any premature gelling due to environmental moisture.
- Handling
To ensure health and safety, Material Safety Data Sheets (MSDS) are available and should be consulted prior to use.
- PACKAGING
- 1500 pounds (680.4 Kg) per box
- 200 pounds (90.7 Kg) per fiber drum
- Foil Sealed Liners.
- Cure
- Moisture Cure
- Technology
- Elastomers
- Certification
Certified Test Results including physical test data are included with each shipment.
Technical data
Table 1 of 3
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Hot Creep Elongation (15 Minutesutes at 250ºC) | 40 | % |
| Specific Gravity | 1.01 | gram/cm3 |
| Tensile Strength | 2800 | psi |
| Hot Creep Elongation (15 Minutesutes at 150ºC) | 60 | % |
| Ultimate Elongation | 450 | % |
Table 2 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Retained Elongation (7 days in 121°C air oven) | 95 | % |
| Retained Elongation (7 days in 158°C air oven) | 95 | % |
| Retained Tensile (7 days in 121°C air oven) | 100 | % |
| Retained Tensile (7 days in 158°C air oven) | 105 | % |
Table 3 of 3
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Cold Bend (at -40°C for 4hrs) | No cracks | — |
| Crush Test | 1300 | lbf |
| Deformation (30 Minutes at 131°C) | 5 | % |
| Dielectric Strength | 850 | V/mil |
| I.R. Constant (at 15.6ºC) | 50000 | MΩ-1000ft |
| Limited Oxygen Index | 25 | % |