SILPURAN® 6700/60 A/B
- Chemical Family
- Silicones
SILPURAN® 6700/60 A/B is a paste-like, easily pigmentable two-component compound with a very short curing time and good mechanical and electrical properties. Vulcanizates are noted for their self-adhesive properties on various substrates. SILPURAN® 6700/60 A/B is designed for medical applications in compliance with the WACKER SILICONES HEALTH CARE POLICY, including implantation for less than 30 days.
Properties
- Physical Form
- Paste
Product families
Applications
Healthcare & Pharma — Medical
- Medical Devices & Assemblies
Product Families
Elastomers — Specialty Elastomers
- Silicone Elastomers
Other characteristics
- Brand
- SILPURAN
- End Uses
- Medical Devices, Medical/Healthcare Applications
- Features
Excellent Surface Properties, Fast Curing, Good Electrical Properties, Good Mechanical Properties, Low VOC, Low Volatility, Pigmentable
- Tear Strength
- 26.0 - 26.0 kN/m
- Processing Methods
- Injection Molding
- Note
Cure conditions: 5 min / 165 °C in press, non post-cured
- Carrier
- Liquid Silicone Rubber (LSR)
- Markets
- Healthcare & Pharma
- Technology
- Elastomers
- Packaging Type
- Pails
- Specific Features
- Self-adhesive
- Reduced volatile content
- Material Features
- Excellent Surface Properties
- Fast Curing
- Good Electrical Properties
- Good Mechanical Properties
- Low VOC
- Low Volatility
- Pigmentable
- Storage Information
Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.
Technical data
Table 1 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 22 hours, 125°C) | 60 | % | DIN ISO 815-1 type B method A |
| Compression Set (at 22 hours, 150°C) | 70 | % | DIN ISO 815-1 type B method A |
| Density | 1.12 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break) | 490 | % | ISO 37 Type 1 |
| Rebound Resilience | 60 | % | ISO 4662 |
| Shore Hardness A | 60 | — | DIN ISO 48-4 |
| Tear Strength | 26 | N/mm | ASTM D 624 B |
| Tensile Strength | 8.2 | N/mm² | ISO 37 Type 1 |
Table 2 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dynamic Viscosity (Shear rate 1 s⁻¹) | 1160000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (Shear rate 10 s⁻¹) | 360000 | mPa·s | DIN EN ISO 3219 |