Dhara Petrochemicals Dpnor UF-M9-010
Dhara Petrochemicals Dpnor UF-M9-010 is modified polyphenylene ether non reinforced flame retardant compounds for injection molding. Dpnor UF-M9-010 is widely used for electricals & electronics applications, appliances applications.This product is available in Natural, Black & other colors.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Polymer Name
- Polyphenylene Ether (PPE)
- Flexural Modulus
- 2550.0 - 2550.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Product Safety
Please refer to the Material Safety Data Sheet for Dpnor Compounds.
- Material Features
- Flame Retardant
- Processing Parameters
- Pre Drying - With a dehumidified air drying equipment at 80~100°C for 2-3 Hours.
- Barrel temperatures
- Feed zone : 250-255°C Compression zone : 255-260°C Front zone : 260-265°C Nozzle : 265-270°C
- Feed zone
- 250-255°C
- Compression zone
- 255-260°C
- Front zone
- 260-265°C
- Nozzle
- 265-270°C
- Mold temperatures
- 80-100°C
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2550 | MPa | ISO 179 |
| Flexural Strength | 95 | MPa | ISO 178 |
| Izod Impact Strength (Notched) at 23 °C | 12 | Kj/m 2 | ASTM D-256 |
| Nominal Tensile Strain | 25 | % | ISO 527 |
| Tensile Strength at Yield | 55 | MPa | ISO 527 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density at 23 °C | 1.08 | g/cc | ISO 1183 |
| Heat Deflection Temperature at 1.82 MPa | 112 | °C | ASTM D-648 |
| Moisture Absorption | 0.07 | % | IS0 62 |
| Moulding Shrinkage | 0.23 | % | ASTM D 955 |
Table 3 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Strength | 25 | kV/mm | IEC 60243 |
| Surface Resistivity | 10^15 | Ohm | IEC 60093 |
| Volume Resistivity | 10^15 | Ohm-cm | IEC 60093 |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability Rating At 0.8 mm Thickness | V0 | mm/mm | UL 94 |
| Flammability Rating At 1.6 mm Thickness | V0 | mm/mm | UL 94 |