Dhara Petrochemicals Dpnor UF-M-012
Dhara Petrochemicals Dpnor UF-M-012 is mPPE Black Compounds, Unfilled for injection molding. Dpnor UF-M-012 is widely used for submersible pump parts like bowls, impellers & diffusers, automotive parts, appliances parts, industrial parts.This product is available in Natural, Black & other colors.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Exterior & Body
- Interior
- Other Automotive Applications
Building & Construction — Building Materials
- Pipes & Plumbing
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Polymer Name
- Polyphenylene Ether (PPE)
- Flexural Modulus
- 2270.23 - 2270.23 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Product Safety
Please refer to the Material Safety Data Sheet for Dpnor Compounds.
- Processing Parameters
- Pre Drying - With a dehumidified air drying equipment at 80~100°C for 2-3 Hours.
- Barrel temperatures
- Feed zone : 250-255°C Compression zone : 255-260°C Front zone : 260-265°C Nozzle : 265-270°C
- Feed zone
- 250-255°C
- Compression zone
- 255-260°C
- Front zone
- 260-265°C
- Nozzle
- 265-270°C
- Mold temperatures
- 80-100°C
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliance Components
- Automotive Components
- Automotive Exterior Parts
- Automotive Interior Parts
- Electric Submersible Pump
- Industrial Parts
- Pump Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 23150 | kg/cm2 | ASTM D-790 |
| Flexural Strength | 575 | kg/cm2 | ASTM D-790 |
| Hardness | 78 | Shore D | ASTM D 2240 |
| Izod Impact Strength (Notched) at 23 °C | 12 | kg . cm/cm | ASTM D-256 |
| Tensile Strength at Yield | 350 | kg/cm2 | ASTM D-638 |
Table 2 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.04 | g/cc | ASTM D792 |
| Heat Deflection Temperature at 18.5 Kg/cm2 | 111 | °C | ASTM D-648 |
| Melt Flow Index at 280 °C /3.8 Kg | 16.83 | g/10 min | ASTM D 1238 |
| Shrinkage (In Flow Direction at3.2 mm Thickness) | 0.65 | % | ASTM D 955 |
| Water Absorption (24 hrs immersion at 23 +/- 1 °C) | 0.12 | % | ASTM D 570 |
Table 3 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability Rating At 3.2 mm Thickness | HB | mm/mm | UL 94 |