Dhara Petrochemicals Dpnor GF-M9-212
Dhara Petrochemicals Dpnor GF-M9-212 is mPPE reinforced with 20% of glass fiber, Flame Retardant Black Compounds for injection molding.Dpnor GF-M9-212 is widely used for electrical & electronic housings, automotive parts.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Exterior & Body
- Interior
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Polymer Name
- Polyphenylene Ether (PPE)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 5736.86 - 5736.86 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Product Safety
Please refer to the Material Safety Data Sheet for Dpnor Compounds.
- Material Features
- Flame Retardant
- Processing Parameters
- Pre Drying - With a dehumidified air drying equipment at 80~100°C for 2-3 Hours.
- Barrel temperatures
- Feed zone : 255-265°C Compression zone : 265-275°C Front zone : 275-280°C Nozzle : 280-290°C
- Feed zone
- 255-265°C
- Compression zone
- 265-275°C
- Front zone
- 275-280°C
- Nozzle
- 280-290°C
- Mold temperatures
- 80-100°C
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Components
- Automotive Exterior Parts
- Automotive Interior Parts
- Electrical Housing
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Abrasion Resistance (CS-17,1000gms,1000 cycles) | 0.03 | gms | ASTM D 1044 |
| Flexural Modulus | 58500 | kg/cm2 | ASTM D-790 |
| Flexural Strength | 1500 | kg/cm2 | ASTM D-790 |
| Hardness | 75 | Shore D | ASTM D 2240 |
| Izod Impact Strength (Notched) at 23 °C | 10 | kg . cm/cm | ASTM D-256 |
| Tensile Strength at Yield | 1050 | kg/cm2 | ASTM D-638 |
Table 2 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.24 | g/cc | ASTM D792 |
| Heat Deflection Temperature at 18.5 Kg/cm2 | 125 | °C | ASTM D-648 |
| Melt Flow Index at 280 °C /3.8 Kg | 5 | g/10 min | ASTM D 1238 |
| Shrinkage (In Flow Direction at3.2 mm Thickness) | 0.23 | % | ASTM D 955 |
| Water Absorption (24 hrs immersion at 23 +/- 1 °C) | 0.1 | % | ASTM D 570 |
Table 3 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability Rating At 3.2 mm Thickness | V0 | mm/mm | UL 94 |