MG Chemicals RTV5818 - Translucent, Very Soft
RTV5810 series sealants are neutral cure, one-component, ready-to-use silicone adhesive sealants that cure to tough resilient silicone rubber on exposure to atmospheric moisture at room temperature. These sealants are fast curing, paste consistency products that may be considered for use where quick initial adhesion build is desired. This may allow for movement of the sealed assemblies in a shorter period of time, increasing productivity.
Properties
- Physical Form
- Paste
Product families
- Caulks & Sealants
Other characteristics
- Cure Method
- Air Dry, Moisture Cure
- Product Type
- 1K (1 component) Adhesive
- Compatible Substrates & Surfaces
Aluminum, Ceramic, Elastomers & Rubbers, Glass, Metal, Plastics, Steel
- Color
- Translucent
- Markets
- Consumer Goods
- Electrical & Electronics
- Cure
- Air Dry
- Moisture Cure
- Technology
- Ready-to-Use Products
- Patent Status
Nothing contained herein shall be construed to imply the nonexistence of any relevant patents or to constitute the permission, inducement or recommendation to practice any invention covered by any patent, without authority from the owner of the patent.
- Packaging Type
- Cartridges
- Labeling Claims
- Non-Corrosive
- Quality Standards
- IPC-CC-830B
Technical data
Table 1 of 7
8 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation | 435 | % |
| Hardness Shore A | 24 | — |
| Peel Strength | 8 (47) | kg/cm (lb/in) |
| Peel Strength (Aluminum) | 8.6 (48) | kg/cm (lb/in) |
| Peel Strength (Glass) | 7.5 (42) | kg/cm (lb/in) |
| Peel Strength (Lexan Polycarbonate) | 7.1 (40) | kg/cm (lb/in) |
| Peel Strength (PVC) | 8.0 (45) | kg/cm (lb/in) |
| Tear Strength | 7.1 (40) | kg/cm (lb/in) |
Table 2 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity | 1.04 | % |
Table 3 of 7
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Coefficient of Thermal Expansion | 15x10⁻⁴ | cm/cm, °C (in/in, °F) |
| Thermal Conductivity | 0.06 | W/(m·K) |
| Thermal Conductivity | -0.1 | (Btu ft/ft2, h, °F) |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Cure Times | 12 | Hours |
Table 5 of 7
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Brittle Point | -60 (-75) | °C (°F) |
| Dielectric Constant (at 100 Hz) | 2.8 | — |
| Dissipation Factor (at 100 Hz) | 2 | — |
| Volume Resistivity | 3x10¹⁵ | ohm-cm |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Dielectric Strength | 17 (425) | kv/mm (v/mil) |
| Tensile Strength | 21 (300) | kg/cm2 (lb/in2)⁽²⁾ |
Table 7 of 7
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Application Rate | 360 | g/min |
| Consistency | Paste | — |
| RTV5813 | Black | — |
| RTV5818 | Translucent | — |
| Tack Free Time | 15 | Minutes |