KRYLEX® KH401
- Chemical Family
- Polyurethanes (PU)
KRYLEX® KH401 is a one component reactive polyurethane hot melt. It is solid at room temperature. This is a low viscosity and temperature adhesive. After being applied warm the product will cool to allow immediate handling. Upon further exposure to ambient humidity KRYLEX® KH401 will achieve high strength bonds and excellent environmental resistance.
Product families
- Hot Melt Adhesives
Other characteristics
- Brand
- KRYLEX
- Product Type
- 1K (1 component) Adhesive, Hot Melt Adhesive
- 1K (1 component) Adhesive
- Hot Melt Adhesive
- Markets
- Adhesives & Sealants
- Storage
Optimal storage conditions are between 15℃ to 30℃ and stored in original sealed foil bag. Storage outside this temperature range can adversely affect product properties and may reduce the stated shelf life.
- Features
After jetting, the glue is smooth on surface.; After jetting, the thickness of the glue line is 0.12mm±0.02mm, and the width is 0.80mm±0.05mm.; Higher green strength with a short or no holding time.; Excellent heat resistance and solvent resistance.; Excellent high temperature and low temperature resistance.
- Applications
Adhesives & Sealants — Other Adhesives & Sealants Applications
- Technology
- Ready-to-Use Products
- Parameter Setting
The following data is the best data obtained from repeated adjustments according to the production requirements. Different users, due to different production equipment, may need to reset some data. The following data is for reference only
- Use Instructions
For best results, ensure parts are clean, dry and free from oil and grease, although good bonds can still be achieved on 'as received' or slightly oily parts. The temperature of substrate should not be lower than 20℃. Low temperature will shorten the open time and cause the bonding failure. If needed, pre-heating of the substrate is recommended. Dispense bead of product onto substrate. Mate opposite substrate within recommended open time. Allow for handling strength to be achieved.
- Ready to Use Product Features
- Excellent Solvent Resistance
- Good Green Strength
- High Strength
- High Temperature Resistance
- Low Temperature Resistant
- Low Viscosity
- Very Good Heat Resistance
Technical data
Table 1 of 1
13 rows| Characteristic | Value | Unit |
|---|---|---|
| Solid Content | 100.0 | % |
| Specific Gravity (25°C) | 1.1 | — |
| Viscosity (Brookfield HBTD 10rpm at 100°C) | 2000±500 | mPa |
| Open Time (1mm line) | 2021-01-02 | minutes |
| Application Temperature | 90-120 | °C |
| Light Blocking | OD Value 3.0 | — |
| Coefficient of Thermal Expansion | 168.2 | μm/ (mK) |
| Coefficient of Thermal Conductivity | 0.32 | W/ (mK) |
| Specific Heat | 2.8 | KJ/ (Kg.K) |
| Elongation at break | min. 650 | % |
| Tensile Modulus | min. 250 | MPa |
| Tensile Strength (1 min) | min. 1.2 | MPa |