ELASTOSIL® M 1470
- Chemical Family
- Silicones
ELASTOSIL® M 1470 is a kneadable, condensation-curing, two-component silicone rubber that vulcanizes at room temperature. This grade is particularly suitable as an impression material for molding models with only a slightly structured surface or for small models with no or only minor undercuts. The process involves impressing a slab of catalyzed rubber onto the model surface or pressing the model into the surface of the rubber slab. ELASTOSIL® M 1470 produces vulcanizates with high hardness and mechanical strength.
Product families
Applications
- Tooling & Moldmaking
Product Families
- Silicone Elastomers
Other characteristics
- Brand
- ELASTOSIL® M
- End Uses
- Modeling Material, Mold Making
- Features
Excellent Mechanical Strength, Fast Curing, Good Sagging Resistance, Heat Resistance, High Hardness, Kneadable, Low Shrinkage, Room Temperature Vulcanizing, Very Good Heat Resistance
- Polymer Name
- Silicone Elastomer
- Tear Strength
- 10.0 - 10.0 kN/m
- Note
Catalyzed with 2 wt% Catalyst Paste T 40, after 4 days at 23°C, 50% relative humidity for catalyzed properties.
- Markets
- Industrial
- Properties
- High Shore A hardness (approx. 45)
- High mechanical strength
- Very good heat resistance
- Low shrinkage
- Cure
- Moisture Cure
- Safety Note
Being a condensation-curing silicone rubber, ELASTOSIL® M 1470 contains only constituents that over many years have proved to be neither toxic nor aggressive. Special handling precautions are therefore not required, i.e., only the general industrial hygiene regulations apply.. Catalyst Paste T 40 contains a tetraorganotin compound, is flammable and may cause irritation in contact with the eyes and skin. Adequate protective measures are required.
- Technology
- Elastomers
- Special Features
- Condensation-curing
- Fast curing
- Heat resistant
- Kneadable
- Non-sag
- Two-component
- Material Features
- Excellent Mechanical Strength
- Fast Curing
- Good Sagging Resistance
- Heat Resistance
- High Hardness
- Kneadable
- Low Shrinkage
- Room Temperature Vulcanizing
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (in water, at 23°C) | 1.28 | g/cm³ | ISO 2781 |
| Elongation (at break) | 230 | % | ISO 37 |
| Linear Shrinkage | 0.2 | % | — |
| Shore Hardness A | 45 | — | ISO 868 |
| Tear Strength | min. 10 | N/mm | ASTM D 624 B |
| Tensile Strength | 4.5 | N/mm² | ISO 37 |
Table 2 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Consistency | Pasty, stiff | — | — |
| Density (at 20°C, 1013 hPa) | approx. 1.28 | g/cm³ | DIN 53217 |