Ecomass® Compound 1002TU77
- Chemical Family
- Polyamides
Ecomass® Compound 1002TU77 is a high-specific-gravity, tungsten powder-filled polyether block amide (PEBA) compound. The processing method for this compound is injection molding/extrusion. It is a nontoxic alternative to lead (Pb) and is used for weighting, balancing, and radiation shielding applications.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Consumer Goods — Sports & Recreation
Healthcare & Pharma — Medical
- Medical Devices & Assemblies
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Composite Materials — Polymers & Resins
- Thermoplastic Resins
Elastomers — Thermoplastic Elastomers
- Thermoplastic Polyamide Elastomers (TPE-A)
Other characteristics
- Brand
- Ecomass
- Density
- 3700.0 - 3700.0 kg/m³
- Polymer Name
- Polyether Block Amide (PEBA)
- Fillers Included
- Tungsten
- Processing Methods
- Extrusion, Injection Molding, Injection Molding
- Markets
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Technology
- Composite Materials
- Elastomers
- Labeling Claims
- Non-Toxic
- Material Features
- Heavy Plastic
- High Density
- High Specific Gravity
- Hot Operating Temperature
- Lead Substitute
- Low Odor
- Non-Toxic
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- EINECS (EU)
- ENCS (Japan)
- IECSC (China)
- ISHL (Japan)
- KECI (Korea)
- PICCS (Phillipines)
- Certifications and Compliance
- RoHS Compliant
- Composites Processing Methods
- Extrusion
- Injection Molding
- Plastics and Elastomers End Uses
- Casino Chips
- Frangible Projectiles
- Golf Club Weights
- Hub Odometer
- Inertia Discs
- Instrument Housing
- Manual Transmission Shifter Cartridge
- Medical Devices
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 3.7 | g/cc | ASTM D792 |
Table 2 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 6 | Mpa | ASTM D638 |
| Tensile Modulus | 26 | Mpa | ASTM D638 |
| Tensile Elongation at Break | min. 500 | % | ASTM D638 |
| Izod Impact Strength, Notched | 67 | J/m | ASTM D256 |
Table 3 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 66 psi) | 52 | °C | ASTM D648 |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity | 0.2 | ohms/sq | ASTM D257 |
Table 5 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Temperature Range | 230 - 260 | °C | — |
| Mold Temperature Range | 65 - 85 | °C | — |
| Mold Shrinkage Rate | 0.7 - 0.8 | % | ASTM D955 |
| Pre-Drying Conditions (at 75°C) | 4 | hrs | — |
Table 6 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Temperature Range | 230 - 260 | °C | — |
| Mold Temperature Range | 65 - 85 | °C | — |
| Mold Shrinkage Rate | 0.7 - 0.8 | % | ASTM D955 |
| Pre-Drying Conditions (at 75°C) | 4 | hrs | — |