Ecomass® Compound 3330CO56 Nat
- Chemical Family
- Polyether Ether Ketone (PEEK)
Ecomass® Compound 3330CO56 Nat is a copper powder-filled Polyetheretherketone (PEEK) compound that is rigid. The processing method for this compound is injection molding/extrusion. It is a nontoxic alternative to lead (Pb) used for weighting and balancing applications. The product form is pellets.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Consumer Goods — Sports & Recreation
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Composite Materials — Polymers & Resins
- Thermoplastic Resins
Other characteristics
- Brand
- Ecomass
- Density
- 2400.0 - 2400.0 kg/m³
- Polymer Name
- Polyetheretherketone (PEEK)
- Fillers Included
- Copper
- Processing Methods
- Extrusion, Injection Molding, Injection Molding
- Markets
- Consumer Goods
- Electrical & Electronics
- Technology
- Composite Materials
- Plastics
- Labeling Claims
- Non-Toxic
- Material Features
- Good Rigidity
- Heavy Plastic
- Hot Operating Temperature
- Lead Substitute
- Medium Density
- Non-Toxic
- Chemical Inventories
- AICS (Australia)
- CSCL (Japan)
- DSL (Canada)
- EINECS (EU)
- IECSC (China)
- KECI (Korea)
- PICCS (Phillipines)
- TSCA (USA)
- Certifications and Compliance
- Japan Chemical Substances Control Law (CSCL)
- RoHS Compliant
- Composites Processing Methods
- Extrusion
- Injection Molding
- Plastics and Elastomers End Uses
- Casino Chips
- Frangible Projectiles
- Golf Club Weights
- Hub Odometer
- Inertia Discs
- Instrument Housing
- Manual Transmission Shifter Cartridge
- Return Weights
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 2.4 | g/cc | ISO 1183 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 78 | MPa | ISO 527 |
| Tensile Modulus | 4900 | MPa | ISO 527 |
| Tensile Elongation at Break | 4 | % | ISO 527 |
| Izod Impact Strength, Notched | 8.3 | KJ/m² | ISO 180 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 66 psi) | 160 | °C | ISO 75 |
| Heat Deflection Temperature (at 264 psi) | 148 | °C | ISO 75 |
Table 4 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Temperature Range | 350 - 370 | °C | — |
| Mold Temperature Range | 165 - 205 | °C | — |
| Mold Shrinkage Rate | 0.8 - 1.1 | % | ISO 294-4 |
| Pre-Drying Conditions (at 150C) | 6 - 8 | hrs | — |
Table 5 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Temperature Range | 350 - 370 | °C | — |
| Mold Temperature Range | 165 - 205 | °C | — |
| Mold Shrinkage Rate | 0.8 - 1.1 | % | ISO 294-4 |
| Pre-Drying Conditions (at 150C) | 6 - 8 | hrs | — |