Ecomass® Compound 4150CO93T1
- Chemical Family
- Polyphenylene Sulfide (PPS)
Ecomass® Compound 4150CO93T1 is a moderate specific gravity, copper powder-filled polyphenylene sulfide (PPS) compound. The processing method for this compound is injection molding. It is a nontoxic alternative to lead (Pb) used for weighting and balancing applications. The product form is pellets.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Consumer Goods — Sports & Recreation
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Composite Materials — Polymers & Resins
- Thermoplastic Resins
Other characteristics
- Brand
- Ecomass
- Density
- 6000.0 - 6000.0 kg/m³
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- Copper
- Processing Methods
- Injection Molding, Injection Molding
- Markets
- Consumer Goods
- Electrical & Electronics
- Technology
- Composite Materials
- Plastics
- Labeling Claims
- Non-Toxic
- Material Features
- Heavy Plastic
- Hot Operating Temperature
- Lead Substitute
- Low Odor
- Medium Density
- Non-Toxic
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- EINECS (EU)
- ENCS (Japan)
- IECSC (China)
- PICCS (Phillipines)
- TSCA (USA)
- Certifications and Compliance
- Korea Toxic Chemicals Control Act (TCCA)
- RoHS Compliant
- Composites Processing Methods
- Injection Molding
- Plastics and Elastomers End Uses
- Casino Chips
- Frangible Projectiles
- Golf Club Weights
- Hub Odometer
- Inertia Discs
- Instrument Housing
- Manual Transmission Shifter Cartridge
- Return Weights
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 6 | g/cc | ASTM D792 |
Table 2 of 4
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 34 | MPa | ASTM D638 |
| Tensile Modulus | 3448 | MPa | ASTM D638 |
| Tensile Elongation at Break | 4 | % | ASTM D638 |
| Flexural Modulus | 3448 | MPa | ASTM D790 |
| Flexural Strength | 41 | MPa | ASTM D790 |
| Izod Impact Strength, Notched | 53 | J/m | ASTM D256 |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 66 psi) | 135 | °C | ASTM D648 |
| Heat Deflection Temperature (at 264 psi) | 127 | °C | ASTM D648 |
Table 4 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Temperature Range | 315 - 345 | °C | — |
| Mold Temperature Range | 135 - 150 | °C | — |
| Mold Shrinkage Rate | 0.8 - 1.0 | % | ASTM D955 |
| Pre-Drying Conditions (at 120°C) | 4 | hrs | — |