CYCOLOY™ FR Resin RCY6214
SABIC's Specialties Business CYCOLOY RCY6214 resin is an injection moldable PC/ABS blend with non-brominated and non-chlorinated flame retardant. It contains 35% post consumer recycle content with a UL-94 V0 rating @ 1.5 mm. Developed for wide variety of applications that require balanced flow and impact performance. Limited availability and restricted color only.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Electrical & Electronic Systems
- Consumer Electronics
- Displays
- Batteries
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Recycled Polymers
- Blends & Alloys
Other characteristics
- Brand
- CYCOLOY™ FR Resin
- Density
- 1180.0 - 1180.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Labeling Claims
Bromine-free, Chlorine-free, Contains PCR Resin, Recyclable, Recycled, Sustainable; Bromine-free; Chlorine-free; Contains PCR Resin; Recyclable; Recycled; Sustainable
- Melt Flow Index
- 21.0 - 21.0 g/10 min
- Processing Methods
- Injection Molding
- Note
ʰ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- UL 94 V0
- UL 94 V1
- Technology
- Plastics
- Additives Included
- Flame Retardant
- Material Features
- Excellent Flowability
- Flame Retardant
- Good Flow
- High Impact Performance
- Non-brominated
- Non-chlorinated
- Recyclable
- Unreinforced
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Camera Applications
- Cell Phones
- Computer Components
- Displays
- EV Battery Modules
- Electrical Components
- Electrical Housing
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 60 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 47 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 4 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 40 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2500 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 90 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2400 | MPa | ASTM D790 |
Table 2 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.18 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.1 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ʰ ¹¹ | 0.4 - 0.6 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ʰ ¹¹ | 0.4 - 0.6 | % | SABIC method |
| Melt Flow Rate (at 260°C, 2.16 kgf) ¹¹ | 21 | g/10 min | ASTM D1238 |
Table 3 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 100 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 85 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 101 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 92 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 60°C, flow) ¹¹ | 0.000071 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 60°C, xflow) ¹¹ | 0.000072 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 85 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 85 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 85 | °C | UL 746B |
Table 4 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hot Wire Ignition (PLC 2) ¹¹ | min. 3 | mm | UL 746A |
Table 5 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 500 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 50 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*3, at 23°C) ¹¹ | 51 | kJ/m² | ISO 180/1A |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 - 90 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.04 | % |
| Melt Temperature ⁷ | 245 - 275 | °C |
| Nozzle Temperature ⁷ | 245 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 245 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 220 - 265 | °C |
| Rear - Zone 1 Temperature ⁷ | 220 - 255 | °C |
| Mold Temperature ⁷ | 60 - 80 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 7 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ᵖ | min. 1.2 | mm | UL 94 |
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.3 | mm | UL 94 |