LNP™ STAT-KON™ Compound DEL329EP
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP™ STAT-KON™ DEL329EP compound is based on Polycarbonate (PC) resin containing 10% carbon fiber, 15% PTFE, Flame Retardant. Added features of this grade include: Electrically Conductive, Internally Lubricated, Flame Retardant, Wear Resistant.
Product families
Applications
- Equipment & Parts
- Industrial Automation
- Semiconductor Manufacturing
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ STAT-KON™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Carbon Fiber, PTFE
- Carbon Fiber
- PTFE
- Flexural Modulus
- 7200.0 - 7200.0 MPa
- Additives Included
Flame Retardant, Lubricant (PTFE), Lubricant (Unspecified); Flame Retardant; Lubricant (PTFE); Lubricant (Unspecified)
- Processing Methods
- Injection Molding
- Note
ᵈ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных изделий и газовое литье. НЕ смешивайте смолу NORYL GTX* с другими марками смол NORYL*. Вторичный полистирол и акрил являются эффективными очищающими материалами. Используйте диапазон температур, подходящий для конкретного очищающего материала. Вторичный материал также необходимо высушить. Максимум 25% вторичного материала. Сушите при рекомендованных температурах и в течение времени для оптимальной производительности. Пересушивание может привести к потере физических свойств и/или появлению дефектов внешнего вида. Не превышайте рекомендованное основное время и температуру сушки выше или:\n4-8 часов при 95°C (200°F), максимум 10 часов\n6-12 часов при 80°C (175°F), максимум 16 часов\n8-16 часов при 65°C (150°F), максимум 24 часа\nИЗБЕГАЙТЕ конвекционных сушильных шкафов. Уровень влажности в нагретом окружающем воздухе может превышать уровень влажности в самой смоле, что приводит к поглощению влаги, а не к сушке. Избегайте температуры расплава выше 300°C (575°F) и времени пребывания более 6-8 минут (может повлиять на свойства и/или внешний вид). Контроль температуры сопла помогает устранить подтекание и преждевременное застывание. Объемы впрыска, превышающие 50% объема цилиндра, могут привести к трудностям в обеспечении постоянного, однородного расплава пластмассы.; ᵍ Измерения проводились на образцах для лабораторных испытаний. Фактическая усадка может отличаться от диапазона из-за различий в условиях переработки, оборудовании, геометрии детали и конструкции пресс-формы. Рекомендуется проводить исследования усадки в пресс-форме с помощью заменителя или предыдущей оснастки перед изготовлением новой пресс-формы для отливаемого изделия.; ᵖ Рейтинги UL, указанные в техническом паспорте, могут не охватывать весь диапазон толщин и цветов. Для получения подробной информации, пожалуйста, обратитесь к желтой карточке UL.; ⁷ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных изделий и газовое литье.; ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Material Features
- ESD Protection
- Electrically Conductive
- Flame Retardant
- Friction Resistant
- Good Moldability
- High Stiffness
- High Strength
- Light Weight
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Electrical/Electronic Applications
- Industrial Applications
- Semiconductor Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 103 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.6 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 8600 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 143 | MPa | ISO 178 |
| Flexural Strain (Break, at 2 mm/min) ¹¹ | 2.5 | % | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 7200 | MPa | ISO 178 |
Table 2 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.1 - 0.3 | % | SABIC method |
| Density ¹¹ | 1.35 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.22 | % | ISO 62-1 |
Table 3 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000018 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000082 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 144 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 140 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 80 | °C | UL 746B |
Table 4 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ᵈ ¹¹ | 100 - 10000 | Ω | ASTM D257 |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 20 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 305 - 325 | °C |
| Front - Zone 3 Temperature ⁷ | 320 - 330 | °C |
| Middle - Zone 2 Temperature ⁷ | 310 - 320 | °C |
| Rear - Zone 1 Temperature ⁷ | 295 - 305 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | 1.5 | mm | UL 94 |