LNP™ STAT-KON™ Compound EE004
- Chemical Family
- Polyetherimide (PEI)Polyimides (PI)
SABIC's Specialties Business LNP STAT-KON EE004 compound is based on Polyetherimide (PEI) resin containing 20% carbon fiber. Added features of this grade include: Electrically Conductive. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Industrial Automation
- Semiconductor Manufacturing
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ STAT-KON™ Compound
- Polymer Name
- Polyether Imide (PEI)
- Fillers Included
- Carbon Fiber
- Flexural Modulus
- 12330.0 - 12330.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵈ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые размеры литниковой системы, литье крупногабаритных деталей, литье тонкостенных изделий и газовое литье. НЕ смешивайте смолу NORYL GTX* с другими марками смол NORYL*. Вторичный полистирол и акриловый пластик являются эффективными материалами для промывки. Используйте диапазон температур, подходящий для конкретного материала для промывки. Вторичный пластик также необходимо высушить. Максимум 25% вторичного пластика. Сушите при рекомендованных температурах и в течение времени для оптимальных характеристик. Пересушивание может привести к потере физических свойств и/или появлению дефектов внешнего вида. Не превышайте рекомендованное основное время сушки и температуру выше или:\n4-8 часов при 95°C (200°F), максимум 10 часов\n6-12 часов при 80°C (175°F), максимум 16 часов\n8-16 часов при 65°C (150°F), максимум 24 часа\nИЗБЕГАЙТЕ конвекционных сушильных шкафов. Уровень влажности в нагретом окружающем воздухе может превышать уровень влажности в самой смоле, что приводит к поглощению влаги, а не к сушке. Избегайте температуры расплава выше 300°C (575°F) и времени пребывания более 6-8 минут (может повлиять на свойства и/или внешний вид). Контроль температуры сопла помогает устранить подтекание и преждевременное застывание. Размеры литниковой системы, превышающие 50% объема цилиндра, могут привести к трудностям в обеспечении постоянного, однородного расплава пластмассы.; ᵍ Измерения выполнены на образце для лабораторных испытаний. Фактическая усадка может отличаться от диапазона из-за различий в условиях переработки, оборудовании, геометрии детали и конструкции пресс-формы. Рекомендуется проводить исследования усадки в пресс-форме с использованием заменителя или предыдущей оснастки перед изготовлением новой пресс-формы для отливаемого изделия.; ᵖ Рейтинги UL, указанные в техническом паспорте, могут не охватывать весь диапазон толщин и цветов. Для получения подробной информации, пожалуйста, обратитесь к желтой карточке UL.; ⁷ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые размеры литниковой системы, литье крупногабаритных деталей, литье тонкостенных изделий и газовое литье.; ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Electrically Conductive
- High Stiffness
- High Strength
- High Temperature Resistance
- Light Weight
- No Added PFAS
- Very Good Heat Resistance
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Electrical/Electronic Applications
- Semiconductor Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 170 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 2 | % | ASTM D638 |
| Flexural Stress ¹¹ | 259 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 12330 | MPa | ASTM D790 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 14800 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 195 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.7 | % | ISO 527 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 12300 | MPa | ISO 178 |
| Flexural Strength (at 2 mm/min) ¹¹ | 264 | MPa | ISO 178 |
Table 2 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.34 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.34 | g/cm³ | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.1 - 0.3 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.1 - 0.3 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.3 - 0.5 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.3 - 0.5 | % | ISO 294 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.2 | % | ISO 62 |
Table 3 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 212 | °C | ASTM D648 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 212 | °C | ISO 75/Af |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 217 | °C | ISO 75/Bf |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00001 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00006 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 1.00E-05 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000047 | 1/°C | ISO 11359-2 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 105 | °C | UL 746B |
Table 4 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ᵈ ¹¹ | 100 - 1000000 | Ω.cm | ASTM D257 |
| Surface Resistivity ᵈ ¹¹ | 100 - 1000000 | Ω | ASTM D257 |
Table 5 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 534 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 58 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 7 | kJ/m² | ISO 180/1A |
Table 6 of 7
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 150 | °C |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 360 - 400 | °C |
| Rear - Zone 1 Temperature ⁷ | 360 - 380 | °C |
| Middle - Zone 2 Temperature ⁷ | 370 - 390 | °C |
| Front - Zone 3 Temperature ⁷ | 380 - 400 | °C |
| Nozzle Temperature ⁷ | 390 - 400 | °C |
| Mold Temperature ⁷ | 140 - 180 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed (Circumferential speed) ⁷ | 0.2 - 0.3 | m/s |
| Vent Depth ⁷ | 0.025 - 0.076 | mm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | 0.5 | mm | UL 94 |