LNP™ STAT-KON™ Compound PX08019
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP STAT-KON PX08019 compound is based on Nylon 6 resin containing carbon fiber and glass fiber. Added features of this grade include: Electrically Conductive, Non-Halogenated Flame Retardant. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Industrial Automation
- Semiconductor Manufacturing
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ STAT-KON™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
Carbon Black, Carbon Fiber, Carbon Powder, Glass Fiber; Carbon Black; Carbon Fiber; Carbon Powder; Glass Fiber
- Flexural Modulus
- 11500.0 - 11500.0 MPa
- Additives Included
- Flame Retardant
- Processing Methods
- Injection Molding
- Note
ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.; ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- ESD Protection
- Electrically Conductive
- Flame Retardant
- High Stiffness
- High Strength
- Light Weight
- No Added PFAS
- Non-Halogenated
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Electrical/Electronic Applications
- Semiconductor Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.33 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 275°C, 2.16 kg) ¹¹ | 10 | cm³/10 min | ISO 1133 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
Table 2 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 160 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2.3 | % | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 230 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 11500 | MPa | ISO 178 |
Table 3 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 207 | °C | ISO 75/Af |
Table 4 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ᵈ ¹¹ | 10000 - 1000000 | Ω | ASTM D257 |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 45 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 7 | kJ/m² | ISO 180/1A |
Table 6 of 7
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 75 - 85 | °C |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Melt Temperature ⁷ | 250 - 270 | °C |
| Front - Zone 3 Temperature ⁷ | 250 - 270 | °C |
| Middle - Zone 2 Temperature ⁷ | 250 - 270 | °C |
| Rear - Zone 1 Temperature ⁷ | 240 - 260 | °C |
| Mold Temperature ⁷ | 70 - 90 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Compliant (94V-0 Flame Class Rating) | 1.6 | mm | UL 94 by SABIC-IP |