LNP™ STAT-KON™ Compound PX05047
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP STAT-KON PX05047 compound is based on Nylon 6 resin containing carbon fiber and glass fiber. Added features of this grade include: Electrically Conductive, High Impact, Heat Stabilized. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Industrial Automation
- Semiconductor Manufacturing
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ STAT-KON™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Carbon Fiber, Glass Fiber
- Carbon Fiber
- Glass Fiber
- Flexural Modulus
- 6000.0 - 6000.0 MPa
- Additives Included
- Heat Stabilizer, Impact Modifier
- Heat Stabilizer
- Impact Modifier
- Processing Methods
- Injection Molding
- Note
ᵈ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных изделий и газовое литье. НЕ смешивайте смолу NORYL GTX* с другими марками смол NORYL*. Вторичный полистирол и акрил являются эффективными материалами для промывки. Используйте диапазон температур, подходящий для конкретной промывочной смолы. Вторичный материал также необходимо высушить. Максимум 25% вторичного материала. Сушите при рекомендованных температурах и времени для оптимальных характеристик. Пересушивание может привести к потере физических свойств и/или появлению дефектов внешнего вида. Не превышайте рекомендованное основное время и температуру сушки:\n4-8 часов при 95°C (200°F), максимум 10 часов\n6-12 часов при 80°C (175°F), максимум 16 часов\n8-16 часов при 65°C (150°F), максимум 24 часа\nИЗБЕГАЙТЕ конвекционных сушильных шкафов. Уровень влаги в нагретом окружающем воздухе может превышать уровень влаги в самой смоле, что приводит к поглощению влаги, а не к сушке. Избегайте температуры расплава выше 300°C (575°F) и времени пребывания более 6-8 минут (может повлиять на свойства и/или внешний вид). Контроль температуры сопла помогает устранить подтекание и преждевременное затвердевание. Объемы впрыска, превышающие 50% объема цилиндра, могут привести к трудностям в обеспечении постоянного, однородного расплава пластмассы.; ᵍ Измерения выполнены на образцах для лабораторных испытаний. Фактическая усадка может отличаться от диапазона из-за различий в условиях переработки, оборудования, геометрии детали и конструкции пресс-формы. Рекомендуется проводить исследования усадки в пресс-форме с помощью заменителя или предыдущей оснастки перед изготовлением новой пресс-формы для отливаемого изделия.; ⁷ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных изделий и газовое литье.; ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Electrically Conductive
- Heat Stabilized
- High Impact Resistance
- High Stiffness
- High Strength
- Impact Modified
- Light Weight
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Electrical/Electronic Applications
- Semiconductor Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 114 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 3.6 | % | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 159 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 6000 | MPa | ISO 178 |
Table 2 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
| Density ¹¹ | 1.17 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 1.5 | % | ISO 62-1 |
Table 3 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000109 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000115 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 214 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 190 | °C | ISO 75/Af |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ᵈ ¹¹ | 1000 - 100000 | Ω | ASTM D257 |
Table 5 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 50 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 12 | kJ/m² | ISO 180/1A |
Table 6 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 265 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 275 - 290 | °C |
| Middle - Zone 2 Temperature ⁷ | 265 - 275 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 260 | °C |
| Mold Temperature ⁷ | 80 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |