LNP™ STAT-KON™ Compound DX10315C

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP™ STAT-KON™ DX10315C compound is based on Polycarbonate (PC) resin containing 15% carbon fiber. Added features of this grade include: LNP Clean Compounding Technology, Low LPC, Low Ionics, Low Outgassing, Low C18-C40 Hydrocarbons, Electrically Conductive.

Product families

Applications

Consumer Goods — Appliances & Electronics

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays
Industrial Automation

Electrical & Electronics — Parts & Components

Connectors
Semiconductor Manufacturing
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ STAT-KON™ Compound
Polymer Name: Polycarbonate (PC)
Fillers Included: Carbon Black, Carbon Fiber, Carbon Powder
Carbon Black
Carbon Fiber
Carbon Powder
Flexural Modulus: 9040.0 - 9040.0 MPa
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.; ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Consumer Goods
Electrical & Electronics
Industrial
Technology: Plastics
Material Features: ESD Protection
Electrically Conductive
Good Mold Release
High Stiffness
High Strength
Light Weight
Low Liquid Particle Count
Low Outgassing
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Cell Phones
Computer Components
Displays
Electrical Components
Electrical/Electronic Applications
Industrial Applications
Semiconductor Applications
Tablets
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	140	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2.7	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	10810	MPa	ASTM D638
Flexural Stress ¹¹	211	MPa	ASTM D790
Flexural Modulus ¹¹	9040	MPa	ASTM D790

Table 2 of 6

4 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.26	—	ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.1 - 0.3	%	SABIC method
Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹	0.1 - 0.3	%	SABIC method
Melt Volume Rate (at 300°C, 5.0 kg) ¹¹	31	cm³/10 min	ISO 1133

Table 3 of 6

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	138	°C	ASTM D648