LNP™ LUBRICOMP™ Compound DP002
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP LUBRICOMP DP002 compound is based on Polycarbonate (PC) resin containing 10% PTFE/silicone. Added features of this grade include: Internally Lubricated, Wear Resistant, Easy Molding,
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- PTFE, PTFE/Silicone, Silicone
- PTFE
- PTFE/Silicone
- Silicone
- Flexural Modulus
- 2100.0 - 2100.0 MPa
- Additives Included
- Lubricant (Unspecified)
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных изделий и газовое литье.; ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.; ᵖ Рейтинги UL, указанные в техническом паспорте, могут не охватывать весь диапазон толщин и цветов. Для получения подробной информации, пожалуйста, обратитесь к карточке UL Yellow Card.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V1
- Technology
- Plastics
- Material Features
- Easy To Mold
- Friction Resistant
- Good Moldability
- Good Processability
- Lubricated
- Unreinforced
- Wear Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 53 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 24.3 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2100 | MPa | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 72 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2100 | MPa | ISO 178 |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.23 | g/cm³ | ISO 1183 |
Table 3 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000072 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000074 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 136 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 125 | °C | ISO 75/Af |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 16 | kJ/m² | ISO 180/1A |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 300 - 315 | °C |
| Front - Zone 3 Temperature ⁷ | 310 - 320 | °C |
| Middle - Zone 2 Temperature ⁷ | 305 - 315 | °C |
| Rear - Zone 1 Temperature ⁷ | 295 - 305 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-1 Flame Class Rating) ᵖ | min. 3 | mm | UL 94 |