LNP™ LUBRICOMP™ Compound JZL012
- Chemical Family
- Polysulfones
SABIC's Specialties Business LNP LUBRICOMP JZL012 compound is based on Polyethersulfone (PES) resin containing proprietary filler and PTFE. Added features of this grade include: Internally Lubricated, Wear Resistant, Dimensional Control.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
- Rail & Mass Transit
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyethersulfone (PES)
- Fillers Included
- Glass Fiber, PTFE, Proprietary
- Glass Fiber
- PTFE
- Proprietary
- Flexural Modulus
- 3100.0 - 3100.0 MPa
- Additives Included
- Lubricant (PTFE), Lubricant (Unspecified)
- Lubricant (PTFE)
- Lubricant (Unspecified)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Dimensional Stability
- Friction Resistant
- High Temperature Resistance
- Low Warpage
- Lubricated
- Very Good Heat Resistance
- Wear Resistant
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 75 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 5 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 3000 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 106 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 3100 | MPa | ISO 178 |
Table 2 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.8 - 1 | % | SABIC method |
| Density ¹¹ | 1.46 | g/cm³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 214 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 199 | °C | ISO 75/Af |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 50 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.05 | % |
| Melt Temperature ⁷ | 355 - 370 | °C |
| Front - Zone 3 Temperature ⁷ | 370 - 380 | °C |
| Middle - Zone 2 Temperature ⁷ | 360 - 370 | °C |
| Rear - Zone 1 Temperature ⁷ | 345 - 355 | °C |
| Mold Temperature ⁷ | 140 - 150 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 60 - 100 | rpm |