LNP™ LUBRICOMP™ Compound FX04491H
- Chemical Family
- PolyethylenesPolyolefins
LNP LUBRICOMP FX04491H compound is based on Polyethylene (PE) resin containing proprietary lubricant. Added features of this grade include: Wear Resistant, Healthcare
Product families
Applications
- Medical Devices & Assemblies
- Surgical Instruments & Trays
- Healthcare Packaging
- Industrial & Transport Packaging
Product Families
- Polyolefins
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyethylene (unspecified)
- Fillers Included
- Proprietary
- Additives Included
- Lubricant (Unspecified)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Lubricated
- Unreinforced
- Wear Resistant
- Plastics and Elastomers End Uses
- Electronic Components
- Medical Devices
- Medical Packaging
- Medical/Healthcare Applications
- Pharmaceutical Packaging
- Surgical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 24 | MPa | ASTM D638 |
| Tensile Strain (Yield) ¹¹ | 7.4 | % | ASTM D638 |
| Flexural Stress ¹¹ | 23 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 10680 | MPa | ASTM D790 |
Table 2 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 0.932 | g/cm³ | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 2.4 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.6 | % | ASTM D955 |
| Wear Factor Washer ¹¹ | 24 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.13 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.11 | — | ASTM D3702 Modified: Manual |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 42 | °C | ASTM D648 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | No break | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 45 | J/m | ASTM D256 |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 230 | °C |
| Front - Zone 3 Temperature ⁷ | 220 - 230 | °C |
| Middle - Zone 2 Temperature ⁷ | 210 - 220 | °C |
| Rear - Zone 1 Temperature ⁷ | 195 - 205 | °C |
| Mold Temperature ⁷ | 40 - 55 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |