LNP™ LUBRICOMP™ Compound DL002

Chemical Family: Polycarbonate (PC)

LNP LUBRICOMP DL002 compound is based on Polycarbonate (PC) resin containing 10% PTFE. Added features of this grade include: Wear Resistant.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polycarbonate (PC)
Fillers Included: PTFE
Flexural Modulus: 2270.0 - 2270.0 MPa
Additives Included: Lubricant (PTFE)
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 HB
UL 94 V1
Technology: Plastics
Material Features: Friction Resistant
Unreinforced
Wear Resistant
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Amusement Machine
Appliances
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

4 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	53	MPa	ASTM D638
Tensile Strain (Break) ¹¹	53	%	ASTM D638
Flexural Stress ¹¹	81	MPa	ASTM D790
Flexural Modulus ¹¹	2270	MPa	ASTM D790

Table 2 of 6

6 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.25	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.7 - 0.9	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.7 - 0.9	%	ASTM D955
Wear Factor Washer ¹¹	97	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	2.80E-01	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.17	—	ASTM D3702 Modified: Manual

Table 3 of 6

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	128	°C	ASTM D648

Table 4 of 6

2 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	No break	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	240	J/m	ASTM D256

Table 5 of 6

10 rows

Characteristic	Value	Unit
Drying Temperature ⁷	120	°C
Drying Time ⁷	4	Hrs
Maximum Moisture Content ⁷	0.02	%
Melt Temperature ⁷	300 - 315	°C
Front - Zone 3 Temperature ⁷	310 - 320	°C
Middle - Zone 2 Temperature ⁷	305 - 315	°C
Rear - Zone 1 Temperature ⁷	295 - 305	°C
Mold Temperature ⁷	80 - 110	°C
Back Pressure ⁷	0.2 - 0.3	MPa
Screw Speed ⁷	30 - 60	rpm

Table 6 of 6