LNP™ LUBRICOMP™ Compound RFP48SXS
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP LUBRICOMP RFP48SXS compound is based on Nylon 6/6 resin containing 40% glass fiber, 20% PTFE/silicone. Added features of this grade include: Heat Stabilized, Wear Resistant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Chassis & Brake
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
Glass Fiber, PTFE, PTFE/Silicone, Silicone, Silicone Oil; Glass Fiber; PTFE; PTFE/Silicone; Silicone; Silicone Oil
- Flexural Modulus
- 8200.0 - 8200.0 MPa
- Additives Included
- Heat Stabilizer, Mold Release Agent
- Heat Stabilizer
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Friction Resistant
- Good Mold Release
- Heat Stabilized
- High Stiffness
- Wear Resistant
- Plastics and Elastomers End Uses
- Appliances
- Brake System
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 155 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.9 | % | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 178 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 8200 | MPa | ISO 178 |
Table 2 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
| Density ¹¹ | 1.6 | g/cm³ | ISO 1183 |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 258 | °C | ISO 75/Af |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 4.00E+01 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Front - Zone 3 Temperature ⁷ | 295 - 305 | °C |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 280 - 305 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 295 | °C |
| Mold Temperature ⁷ | 95 - 110 | °C |
| Rear - Zone 1 Temperature ⁷ | 265 - 275 | °C |
| Screw Speed ⁷ | 30 - 60 | rpm |